Treatment of PET Nonwoven with a Water Vapor or Carbon Dioxide Plasma

AJA Klomp,JGA Terlingen,GAJ Takens,A Strikker,GHM Engbers,J Feijen
DOI: https://doi.org/10.1002/(sici)1097-4628(20000124)75:4<480::aid-app3>3.0.co;2-9
IF: 3
2000-01-01
Journal of Applied Polymer Science
Abstract:Gas plasma treatment of poly(ethylene terephthalate) nonwoven (NW-PET) was used to increase the hydrophilicity of single- and multilayer NW-PET. NW-PET was treated with a pulsatile CO2 or with a pulsatile H2O glow discharge. X-ray photoelectron spectroscopy (XPS) showed significantly more oxygen with CO2 glow-discharge-treated NW-PET than with H2O glow-discharge-treated-NW-PET surfaces. Moreover, the introduction rate of oxygen at a single layer of NW-PET was higher for a CO2 than for a H2O glow-discharge treatment. Titration data revealed significantly higher surface concentrations of carboxylic groups for CO2 glow-discharge NW-PET than for H2O glow-discharge-treated NW-PET. Mass spectrometry analysis revealed that the entire internal surface of a single layer of NW-PET was modified. XPS and contact measurements confirmed the modification of the internal surface of multilayers of NW-PET. H2O and CO2 glow-discharge-treated substrates consisting of six layers of NW-PET had a nonuniform surface concentration of carboxylic acid groups as determined with titration experiments, The outside layers of the substrate contained a higher surface concentration of carboxylic acid groups than did the inside layers;XPS analysis and titration data showed that the rinsing of H2O and CO2 glow-discharge-treated NW-PET with water changed the surface composition considerably. Part of the carboxylic acid group-containing species were washed off (C) 2000 John Wiley & Sons, Inc.
What problem does this paper attempt to address?