Abstract:Type II samples were obtained from the adjacent positions of pyramidal sector and prismatic sector in the same potassium dihydrogen phosphate (KDP) single crystal grown by the "point seed" technique under different temperature range and supersaturation. Some samples were annealed at 160 degrees C for 24 h. The UV-Vis spectra, especially in the ultraviolet region, show the optimal transmitting ability for the KDP crystal which was grown under relative low temperature range. The structural analysis performed by means of Fourier transformed infrared spectroscopy (FTIR) suggests that the crystal lattice of the KDP grown under relative small supersaturation become compact at the molecular level. The results of photoluminescence (PL) emission spectra show that the PL intensity increases with the rise of supersaturation and growth temperature range, which indicates that the concentration of all the detected micro defects in the KDP is abundant. The damage threshold conducted using 532 nm ns laser pulses shows the same trend with the results of PL spectra. The laser-induced damage threshold (LIDT) has been improved with the decrease of growth temperature range and supersaturation, and its variation has the highest correlation with the concentration of hydrogen vacancy defect. In addition, thermal annealing can effectively reduce the concentration of all the detected micro defects in the sample, and LIDT of the samples can be enhanced further after laser sub-threshold annealing.

Study on K(DxH1-x)2PO4 Crystals: Growth Habit, Optical Properties and Their Improvement by Thermal-Conditioning

Improvement of the bulk laser damage threshold of potassium dihydrogen phosphate crystals by reducing the organic impurities in growth solution

Polymorphism and metastable growth of DKDP

Growth and Characterization of L-phenylalanine Doped KDP Crystals

Study on optical performance and 532 nm laser damage of rapidly grown KDP crystals

Study on Micro Morphology of Potassium Dihydrogen Phosphate Crystals Grown at Elevated Temperatures

EFFECTS OF GROWTH METHOD ON THE GROWTH HABIT AND OPTICAL PROPERTY OF DKDP CRYSTALS

Effect of Raw Material and Growth Method on Optical Properties of Dkdp Crystal

Nonlinear optical refraction characteristics of rapidly grown K(D x H1− x )2PO4 crystals

Influence of MoO42- on crystalline perfection and optical properties of potassium dihydrogen phosphate (KDP) crystal

Nonlinear optical refraction characteristics of rapidly grown K(D<i><sub>x</sub></i>H<sub>1−</sub><i><sub>x</sub></i>)<sub>2</sub>PO<sub>4</sub>crystals

Study on the Properties of the DKDP Crystal with Different Deuterium Content

Growth, Structural And Optical Properties Of 12%-Deuterated Kdp Crystals

Crystalline Perfection and Optical Properties of Rapid Grown Kh2po4 Crystal with Chromate Additive

Crystal Growth and Characterization of Non-Centrosysmmetric Polyphosphates, Type Iii Knd(Po3)(4) and Kgd(Po3)(4)

Characteristics of Nonlinear Optical Absorption and Refraction for Kdp and Dkdp Crystals

Study on Optical Property of Rapid Growth KDP and DKDP Crystals

Effect of Deuterium Content on the Structural, Optical, and Thermal Properties of DKDP Crystals: a Systematic Analysis

Effect of DTPA on Rapid Growth and Performance of KDP Crystal

The Effect of Material, Thermal and Laser Conditioning on the Damage Threshold of Type Ii Tripler-Cut Dkdp Crystals

Effect of Deuterium Content on the Optical Properties of DKDP Crystals