SYNTHESIS AND CHARACTERIZATION OF BRANCHED COPOLYSILANES OF HIGH MOLECULAR WEIGHT
ZJ Peng,WJ Si,HJ Fu,HM Zeng,HZ Miao
DOI: https://doi.org/10.3321/j.issn:1000-3304.2002.03.009
2002-01-01
Acta Polymerica Sinica
Abstract:According to the mechanism of hydrosilylation, the process of "normal-sequence-dripping mode" was designed. And using such process, the monomers of dichloromethylphenethylsilane and dichloromethyl (n) hexylsilane were synthesized with high productivity ( the maximal productivity of dichloromethylphenethylsilane, 88% and dichloromethyl-n-hexylsilane, 96.2%) and low pollution (minute quantity of fumes in off-gas) By Wurtz reductive coupling reaction of dichlorosilane ( dichloromethylphenethylsilane and dichloromethyl ( n) hexylsilane) and trichlorosilane (trichloromethylsilane and trichlorophenylsilane), four series of two-dimensionally branched copolysilanes were designed and synthesized using the two procedures of "pre-polymerization" and "mixed-polymerization" with or without diglyme. The polymers are polymethylphenethylsilene-co-methylsilynes, polymethyl-phenethylsilene-co-phenylsilynes, polymethyl-n-hexylsilene-co-methylsilynes, and polymethyl-n-hexylsilene-co-phenylsilynes. Through the characterization of GPC, UV, H-1-NMR and Si-29-NMR, the properties of such copolysilanes were determined. The effects of such factors as monomer characteristics, co-polymerization ratio (D/T), co-polymerization mode("pre-polymerization" and "mixed-polymerization") solvent additive (diglyme) and reaction time on the polymer properties, such as productivity. molecular weight and UV absorption spectra, were studied and discussed. It was discovered that the branched copolysilanes of very high molecular weight with highly bulky substituents could be obtained with "pre-polymerization". The maximum of the molecular weight of such branched copolysilanes could reach 2.8 x 10(5), which was at least ten times as those of the branched copolysilanes derived from the mixed-polymerization procedure. The mechanism of increasing the molecular weights of branched copolysilanes was proposed.