Abstract:The friction is the considerable boundary condition in bulk metal forming.In this paper,the ring compression test was used to evaluate the friction coefficient and factor in Coulomb friction model and Tresca friction model for the plastic deformation of aluminum alloy AA5052.The micro-macro analysis method combining surface morphology and micro-texture was used to explore the friction behaviors in AA5052 cold forming process.In general,the magnitude(μ or m) of friction changes before and after a deformation threshold during ring compression.The maximum change rate of the magnitude(μ or m) before and after the deformation threshold is close to 18.5% under the present experimental conditions,and the change rate decreases with increasing loading speed.The lubrication using MoS 2 is better than that using oil at lower speeds(0.15 mm/s,1.5 mm/s),but the lubrications for MoS 2 and oil are similar at higher speeds(15 mm/s).The surface roughness,three-dimensional topography,and surface texture of compressed ring have a sudden change around the deformation threshold,which deviate from the previous evolution trend.The increased friction after deformation threshold also promotes the formation of sufficient shear strain layer in the subsurface plane of the compressed ring,and then it hinders the formation of the typical deformation textures with β-oriented line and promotes the appearance of shear textures such as {001}(110),{111}(uvw) and {hkl}{110)textures.

Investigation of the Diffluence Mechanism of an Aluminium Alloy Ring under Compression

Diffluence Behaviour of Aluminium Alloy During Ring Compression

Deformation Rule and Mechanism in Compress Process of Aluminium Alloy Square Ring

Frictional Behavior During Cold Ring Compression Process of Aluminum Alloy 5052

Deformation Behaviour of the Compressed Square Ring of 7075 Aluminium Alloy

Influences of Initial Porosity, Stress Triaxiality and Lode Parameter on Plastic Deformation and Ductile Fracture

Study on the Thermo-compression Deformability Rule of Aluminum Alloy Ring under Partial Restriction

Deformation Behavior in the Compression Process of L-shaped Aluminum Alloy Components

Deformation Modes Coupled Analysis in the Forging Process of Disc-Shaped Components

Coupling Deformation of Aluminum Alloy Disk Components During Forging Process

Investigation of Interfacial Friction and Inverse Flowing Behavior under the Adhesive State

Finite element analysis and experimental investigation of the hydrostatic extrusion process of deforming two-layer Cu/Al composite

Evaluation of the measurement of metal flow and strain distribution in bulk metal forming

Experimental and Finite Element Analysis of Flow Behavior of 2A14 Aluminum Alloy During Multi-directional Forging

Effect of Friction Condition on Flow Behavior of Aluminum Alloys During Extrusion

Research on machining deformation of aluminum alloy rolled ring induced by residual stress

Investigation of an L-Shaped Cross-Sectioned AA6061 Aluminum Alloy Ring via Extrusion and Self-Bending Integral Processing Technology

Compressive Formability of 7075 Aluminum Alloy Rings under Hydrostatic Pressure

Investigation of the Flange Earring of Deep-Drawing Aluminum Sheets by Rate-Independent Polycrystalline Plasticity Finite Element Analysis

Residual Stress Analysis of a 2219 Aluminum Alloy Ring Using the Indentation Strain-Gauge Method

Analysis of Metal Deformed Flow under Adhesive Friction by Ring Upsetting