Abstract:Mesoporous silica with Ia (3) over bard structure has been successfully prepared by using mixed surfactants of commercially available nonionic block copolymer P123 (EO(20)PO(70)EO(20)) and anionic sodium dodecyl sulfate (SDS) as structure-directing agents through an acid-catalyzed silica sol-gel process. XRD, TEM, and N(2) sorption measurements show that the products have highly ordered bicontinuous cubic mesostructure with high surface area (similar to 770 m(2)/g), large pore volume (similar to 1.5 cm(3)/g) and uniform pore size (similar to 10 nm). Effects of preparation parameters on the formation of the mesostructure have been extensively investigated. It is found that the molar ratios of SDS/P123 between 2.1 and 2.5 and that of silicic species to P123 in the range from 40 to 75 are favorable for the formation of highly ordered Ia (3) over bard mesostructure. Prolonging hydrothermal treatment time leads to almost unchanged cell parameters of the products, whereas there is obvious increase of the pore sizes and pore volume. The results show that resultant template-free mesoporous silica products have excellent thermal stability, and they are more stable in N2 atmosphere than in air. Morphologies of the resultant materials can be further controlled by adding inorganic salt (such as Na(2)SO(4)) into the mixed surfactants system. Coral- and petaline-like mesoporous silica with continuous skeletons can be obtained. Understanding this synthesis system might be useful for economical and large-scale production of mesoporous materials with controllable structures.

Synthesis and characterization of chiral periodic mesoporous organosilicas.

Bifunctional Hybrid Mesoporous Organoaluminosilicates with Molecularly Ordered Ethylene Groups.

Chiral mesostructured silica nanofibers of MCM-41.

Room-Temperature Synthesis in Acidic Media of Large-Pore Three-Dimensional Bicontinuous Mesoporous Silica with Ia3d Symmetry

Synthesis and Characterization of Functionalized Mesoporous Ethanesilica

Synthesis and characterization of mesoporous and amorphous silica modified with silica-organo-sulfogroups

Organic Groups Functionalised Mesoporous Silicates

Mesoscopically Ordered Organosilica and Carbon-Silica Hybrids with Uniform Morphology by Surfactant-Assisted Self-Assembly of Organo Bis-Silanetriols.

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Synthesis of Periodic Mesoporous Organosilicas with Chemically Active Bridging Groups and High Loadings of Thiol Groups

High‐Temperature Generalized Synthesis of Stable Ordered Mesoporous Silica‐Based Materials by Using Fluorocarbon–Hydrocarbon Surfactant Mixtures

Synthesis of Dual‐Mesoporous Silica Using Non‐Ionic Diblock Copolymer and Cationic Surfactant As Co‐Templates

Synthesis, Bifunctionalization, and Application of Isocyanurate-Based Periodic Mesoporous Organosilicas

Self-Directed Assembly Of Organosilanes Into Helically Mesoporous Nanocomposites

Synthesis of Large‐Pore Ia$\bar3$d Mesoporous Silica and Its Tubelike Carbon Replica

Periodic Mesoporous Organosilica Materials: Self-Assembly of Carbamothioic Acid-Bridged Organosilane Precursors.

Synthesis of Large-Pore Urea-Bridged Periodic Mesoporous Organosilicas

Synthesis and characterization of macroporous silica modified with optically active poly[N- (oxazolinylphenyl)acrylamide] derivatives for potential application as chiral stationary phases

Facile Synthesis And Chiral Separation Of Chiral Mesoporous Silica Microspheres

Chirality induction to porphyrin derivatives co-confined at the air-water interface with silica nano-helices: towards enantioselective thin solid film surfaces