Abstract:The processing of cross-linked polyarylene ether nitrile (PEN), which has a triazine rings structure, has been investigated under different reaction times and temperatures. In this study, the PEN films prepared by the tape-casting formed the thermally stable triazine rings by catalytic cross-linking reaction gradually, which was characterized by Fourier transform infrared spectroscopy. The chemical cross-linking reaction occurred as the CN group absorption of PEN at 2221 cm(-1) decreased and a new absorption peak, at 1682 cm(-1), was observed, and the absorption peak intensity would be progressively larger, with the extension of the processing time. After the formation of cross-linking networks, the cross-linking degree and thermal and mechanical properties of the processed films were improved substantially, compared with the untreated films. The film with added ZnCl2 as the catalyst was more rapidly cross-linked, and its properties were better than that without catalyst at the same treatment conditions. The glass-transition temperature (T-g) of PEN films processed at 350 degrees C for 4 h (213.65 degrees C) was higher than that of PEN films before the treatment (161 degrees C), and the tensile strength was also improved significantly. The PEN was processed at 350 degrees C for 2 h, whose initial decomposition temperature increases by about 10 degrees C, compared with that of untreated film, at one time. The rheology behavior of the cross-linked films was processed on dynamic rheometer to monitor and track the process of polymer cross-linking reaction. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 120: 1822-1828, 2011

Thermal crosslinking behavior of poly (aryl ether ketone) copolymers containing naphthalene moieties

Study on Synthesis and Thermal Property of Epoxy Resin Containing Naphthalene

Thermal Decomposition Behavior of Naphthalene-Labeled Polyethylene

The Synthesis and Characterization of a New Cross-Linkable Copolymerization Poly(arylene Ether Sulfone) End-Capped with Phthalonitrile

Synthesis and Thermal Properties of Crosslinkable Alternating Poly(aryl ether ketone)s Containing Pendant Phenylethynyl Groups

Thermal Degradation Behaviors of Poly (arylene Ether Nitrile) Bearing Pendant Carboxyl Groups

Crosslinking behavior of polyarylene ether nitrile terminated with phthalonitrile (PEN-t-Ph)/1,3,5-Tri-(3,4-dicyanophenoxy) benzene (TPh) system and its enhanced thermal stability

Synthesis and properties of polyarylene ether nitrile random copolymer containing naphthalene and biphenyl structure

Thermal degradation kinetics of poly(arylene ether nitrile) and its cross-linked polymer

The influence of cross-linking reaction on the mechanical and thermal properties of polyarylene ether nitrile

Synthesis and Properties of Semicrystalline Poly(ether nitrile ketone) Copolymers

Preparation and physical properties of intrinsic low-k polyarylene ether nitrile with enhanced thermo-stability

Crosslinkable poly(aryl ether ketone)s containing pendant phenylethynyl moieties: Synthesis, characterization and properties

Study of Crosslinking of Polyphosphazene with Allyl Pendant Groups Initiated by Benzoyl Peroxide

Electrochemical Copolymerization and Stability of Crosslinked Bis[1,2‐(pyrrol)ethoxy]ethane with Pyrrole

Synthesis and Characterization of N-Substituted Polyether-Block-Amide Copolymers

X-ray photoelectron spectroscopy investigation into thermal degradation and stabilization of polyacrylonitrile fibers

Synthesis and Properties of Crosslinked Poly(arylene Ether Nitriles) Containing Pendant Phthalonitrile

Preparation and performance of soluble N-heterocyclic poly(aryl ether ketone)s with enhanced thermal resistance

Synthesis and Properties of Cross-Linkable Poly(Arylene Ether Nitrile)S Containing Side Propenyl Groups

Copolymers of poly(aryl ether ketone)/poly(ether ether amide) containing different numbers of methylene in the main chain: Synthesis and properties