Abstract:A series of wholly aromatic copolyesters P-IPAx with low melting point (Tm) derived from hydroxybenzoic acid (HBA), 6-hydroxy-2-naphthoic acid (HNA), 4,4'-dihydroxy-biphenyl (BP), terephthalic acid (TPA) and isophthalic acid (IPA) was synthesized by melt polymerization. The copolyesters were characterized by Thermogravimetric Analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (XRD), polarized optical microscopy and mechanical strength measurements. The addition of BP/TPA resulted in a decrease in Tm for the copolyester from 280.7 to 218.7°C compared to the parent copolyester P-HBA73 (HBA/HNA copolymer). As the amount of added IPA was increased, Tm decreased, and when the IPA concentration exceeded 5 mol%, the Tm peak in the DSC was not observed and the glass transition temperature was confirmed. The XRD analysis showed that the crystallinity decreased with increasing IPA concentration, but the ability to form a nematic liquid crystal phase was maintained based on observations by polarizing optical microscopy. In terms of the mechanical properties, there was a decrease in tensile strength but an increase in the modulus of elasticity. The copolymer with 10 mol% IPA could be molded at a relatively low temperature (about 200 °C). The addition of BP/IPA units improved the material processability while maintaining the characteristics typical of wholly aromatic LCPs (especially the modulus). It was also shown that the product could be processed at a lower temperature compared to commercially available wholly aromatic LCPs. Access to a wider range of processing temperatures will contribute to an expansion of applications for wholly aromatic LCPs.

Synthesis and properties of high performance aromatic thermotropic liquid crystal copolyesters based on naphthalene ring structure

Study on Synthesis and Thermal Property of Epoxy Resin Containing Naphthalene

2,2‐Bistrifluoromethyl‐4,5‐difluoro‐1,3‐dioxole‐co‐tetrafluoroethylene Copolymers with Different Compositions: Synthesis, Chain and Condensed Matter Structures and Optical Properties

Effect of Monomer Structure on Crystallization and Glass Transition of Flexible Copolyesters

Synthesis and properties of wholly aromatic phosphorus-containing thermotropic liquid crystal copolyesters with excellent fibre formation ability

Synthesis and structure-property relationship of thermotropic liquid crystalline polyesters containing thiophene-aromatic and cycloaliphatic moieties

Characterization and mechanical strength of wholly aromatic liquid crystalline polymers with low melting point

Synthesis and characterization of fully aromatic thermotropic liquid-crystalline copolyesters containing m-hydroxybenzoic acid units

Synthesis and characterization of thermotropic liquid crystalline copolyester containing bis(4-hydroxyphenyl) methanone series (I)

X-ray studies of the structure of thermotropic copolyesters

The structure of liquid crystalline aromatic copolyesters prepared from 4-hydroxybenzoic acid and 2-hydroxy-6-naphthoic acid

Solid-state structures and thermal properties of aliphatic–aromatic poly(butylene adipate-co-butylene terephthalate) copolyesters

Annealing effect of thermotropic liquid crystalline copolyester fibers on thermo-mechanical properties and morphology

Synthesis and Properties of Low Dielectric Thermotropic Liquid Crystal Polyarylates

Synthesis Of Diacetylene-Containing Copolyesters And Their Effect On Electro-Optical Properties Of Liquid Crystals

Synthesis of A Novel Liquid Crystalline Copolyester with Fractile Structure

SYNTHESIS AND CHARACTERIZATION OF MAIN CHAIN AROMATIC LIQUID CRYSTAL COPOLYESTERS WITH X-SHAPED AND ROD-SHAPED MESOGENIC UNITS *

SYNTHESIS AND CHARACTERIZATION OF THERMOTROPIC POLYAMIDE LIQUID CRYSTALLINE BLOCK COPOLYMERS

Dependence of the Physical Properties and Molecular Dynamics of Thermotropic Liquid Crystalline Copolyesters on p-Hydroxybenzoic Acid Content

Synthesis and Characterization of Liquid Crystalline Copolyesters Containing Horizontal and Lateral Rods in Main Chain

Synthesis and Properties of Thermotropic Liquid Crystalline Copolyesters Containing p‐Hydroxyphenylacetic Acid and m‐Hydroxybenzoic Acid Units