Abstract:A one-step colloidal process has been adopted to prepare silver (Ag) and silver sulfide (Ag2S) nanocrystals, thus avoiding presynthesis of an organometallic precursor and the injection of a toxic phosphine agent. During the reaction, a layered intermediate compound is first formed, which then acts as a precursor, decomposing into the nanocrystals. The composition of the as-obtained products can be controlled by selective cleavage of S–C bonds or Ag–S bonds. Pure Ag2S nanocrystals can be obtained by directly heating silver acetate (Ag(OAc)) and n-dodecanethiol (DDT) at 200 ° C without any surfactant, and pure Ag nanocrystals can be synthesized successfully if the reaction temperature is reduced to 190 ° C and the amount of DDT is decreased to 1 ml in the presence of a non-coordinating organic solvent (1-octadecene, ODE). Otherwise, the mixture of Ag and Ag2S is obtained by directly heating Ag(OAc) in DDT by increasing the reaction temperature or in a mixture of DDT and ODE at 200 ° C. The formation mechanism has been discussed in detail in terms of selective S–C and Ag–S bond dissociation due to the nucleophilic attack of DDT and the lower bonding energy of Ag–S. Interestingly, some products can easily self-assemble into two- or three-dimensional (2D or 3D) highly ordered superlattice structures on a copper grid without any additional steps. The excess DDT plays a key role in the superlattice structure due to the bundling and interdigitation of the thiolate molecules adsorbed on the as-obtained nanocrystals.

Synthesis of Faceted and Cubic Ag2S Nanocrystals in Aqueous Solutions.

L-Cysteine-Assisted Synthesis and Optical Properties of Ag2s Nanospheres

Synthesis of Nanocrystalline Ag2S in Aqueous Solution

Sonochemical Synthesis of Amorphous Long Silver Sulfide Nanowires

A Dry Method To Synthesize Dendritic Ag2se Nanostructures Utilizing Cdse Quantum Dots And Ag Thin Films

Synthesis of Hierarchical CuS Flower-Like Submicrospheres Via an Ionic Liquid-Assisted Route

‘One-Step’ Controllable Synthesis of Ag and Ag2S Nanocrystals on a Large Scale

Selected Synthesis of CuS Nanotubes and Hollow Nanospheres at Room Temperature.

Controlled synthesis and self-assembly of highly monodisperse Ag and Ag2S nanocrystals

Thiamine-assisted Hydrothermal Synthesis of Ag2S Microcrystals and Their Optical Properties

Shape-controlled Synthesis and Formation Mechanism of Nanoparticles-Assembled Ag2S Nanorods and Nanotubes

Synthesis and characterization of Ag2S nanocrystals with different morphologies in micromicelles

The synthesis and characterization of nanocrystalline Cu- and Ag-based multinary sulfide semiconductors

Facile Synthesis of Silver Nanocubes with Sharp Corners and Edges in an Aqueous Solution

Synthesis of Sers Active Ag2s Nanocrystals Using Oleylamine As Solvent, Reducing Agent and Stabilizer

A Novel One-Step Solvothermal Route to Nanocrystalline CuSbS2 and Ag3SbS3

Controllable Synthesis of Floatable Nanocrystalline Ag2S and Ag by a Silane Coupling Agent-Modified Solvothermal Method

Polyol mediated synthesis of nanocrystalline M3SbS3 ( M = Ag, Cu)

Controlled synthesis and optical properties of the semiconductor Ag2S nanotubes

A Novel Solid–liquid Route for the Preparation of Cu3Se2 and Ag2Se Nanocrystals

Controllable Synthesis of Silver and Silver Sulfide Nanocrystals Via Selective Cleavage of Chemical Bonds