Abstract:A novel in situ autoreduction route has been developed, by which monodispersed silver nanoparticles with tunable sizes could be easily fabricated on silica-based materials, especially inside the channels of mesoporous silica (MPS). 13C CP/MAS NMR spectroscopy was employed to monitor the whole assembly process. It was demonstrated that the amino groups of APTS (aminopropyltriethoxyl silane)-modified MPS can be used to anchor formaldehyde to form novel reducing species (NHCH2OH), on which Ag(NH3)2NO3 could be in situ reduced. Monodispersed silver nanoparticles were thus obtained. In situ XRD and in situ TEM experiments were used to investigate and compare the thermal stabilities of silver nanoparticles on the external surface of silica gels (unconfined) and those located inside the channels of SBA-15 (confined). It was observed that unconfined silver nanoparticles tended to agglomerate at low temperatures (i.e., lower than 773 K). The aggregation of silver nanoparticles became more serious at 773 K. However, for those confined silver nanoparticles, no coarsening process was observed at 773 K, much higher than its Tammann temperature (i.e., 617 K). Only when the treating temperature was higher than 873 K could the agglomeration of those confined silver nanoparticles happen with time-varying via the Ostwald ripening process. The confinement of mesopores played a key role in improving the thermal stabilities of silver nanoparticles (stable up to 773 K without any observable coarsening), which is essential to the further investigations on their chemical (e.g., catalytic) properties.

Controllable Synthesis of Floatable Nanocrystalline Ag2S and Ag by a Silane Coupling Agent-Modified Solvothermal Method

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

Sol-gel Preparation of Ag-silica Nanocomposite with High Electrical Conductivity

Controlled synthesis and self-assembly of highly monodisperse Ag and Ag2S nanocrystals

Synthesis of Nanocrystalline Ag2S in Aqueous Solution

‘One-Step’ Controllable Synthesis of Ag and Ag2S Nanocrystals on a Large Scale

A Controlling Method For Agi Nanoparticles Preparation Using Combinatorial Surfactants

Controllable Synthesis of Silver and Silver Sulfide Nanocrystals Via Selective Cleavage of Chemical Bonds

Halloysite Nanotube Supported Ag Nanoparticles Heteroarchitectures As Catalysts for Polymerization of Alkylsilanes to Superhydrophobic Silanol/siloxane Composite Microspheres

Size-Controlled Synthesis of Highly Water-Soluble Silver Nanocrystals

Confination of Ag Nanostructures Within SBA-15 by a “two Solvents” Reduction Technique

Converting ultrafine silver nanoclusters to monodisperse silver sulfide nanoparticles via a reversible phase transfer protocol

Selective Sulfuration at the Corner Sites of a Silver Nanocrystal and Its Use in Stabilization of the Shape

Controllable Synthesis and Surface Wettability of Flower-Shaped Ag Nanocube-Organosilica Hybrid Colloidal Nanoparticles.

Controlled synthesis of monodisperse silver nanocubes via a solvothermal method

A Facile Route to Well-Dispersed Single-Crystal Silver Nanoparticles from [agso3]− in Water

In-Situ Preparation of Surface-Functionalized Sio2 Nanoparticles with Controllable Sizes

Controlled Synthesis of Ag Nanowires and Nanoparticles in Mesoporous Silica Using Supercritical Carbon Dioxide and Co-Solvent

Toward Monodispersed Silver Nanoparticles with Unusual Thermal Stability.

Elucidation of the capillarity-promoted sintering of silver nanoparticles produced by a spark ablation vapor source