Abstract:A systematic study of Pb-doping and annealing effects in vacuum (2 x 10(-3) Pa) on T, and the microstructure of Bi2-xPbxSr2CaCu2Odelta compounds has been carried out. It is found that the structure belongs to the Bi-2212 phase. The c-and b-axes almost keep unchanged while Bi is replaced by Pb. With increasing annealing temperature, c- and b-axis parameters monotonically increase while the a-axis parameter is unchanged. The modulated period becomes longer and finally disappears with increasing Pb content and annealing temperature. Meanwhile, the distortion of CuO2 planes becomes serious. There is an optimum T, with increasing annealing temperature, which reveals that the carrier concentration p changes from overdoped to underdoped. It is suggested that the differences of both the valences and the ionic sizes of Pb2+ and Bi3+ cause the reduction of extra oxygen, resulting in the increasing positive charge in the BiO double planes. The distortion of CuO2 planes is partially caused by the increase of positive charge in BiO double planes. A charge-transfer between the carrier reservoir (BiO-SrO) and the conducting CuO2 plane is induced by Pb-doping and annealing in vacuum. Both the distortion of CuO2 planes and the charge-transfer control the carrier concentration and carrier distribution in CuO2 planes, which is related to the superconductivity of the Pb-doped Bi-2212 phase.

Effect of Bi/Pb Ratio and Annealing Temperature on T C and Formation of High- T C Phase in Bi-Pb-Sr-Ca-Cu-O Superconductor

Preparation and Superconductivity of the High-Tc Phase of Pb-doped Bi-Sr-Ca-Cu-O Superconductor

Effect of Pb-doping and annealing on the structure and Tc of Bi-2212 phase superconductor

HIGH Tc SUPERCONDUCTIVITY AND SUBSTRUCTURE OF Bi-Sr-Ca-Cu-O SYSTEM

HIGH T<sub>c</sub> SUPERCONDUCTIVITY AND SUBSTRUCTURE OF <font>Bi-Sr-Ca-Cu-O</font> SYSTEM

47 K superconductivity in Bi1.6Pb0.4Sr1.65La0.35CuOz

STUDY ON THE HIGH TEMPERATURE RESISTIVITY OF Bi 1.6 Pb 0.4 Sr 2ca 2cu 3O X

Preparation of 110k Superconductor in Bi-Sr-Ca-Cu-O System

Superconductivity and Crystal Structure in the Bi-Pb-Sr-Ca-Cu-O System

Preparative And Structural Studies On The Superconducting Phase (Bi1.7pb0.2in0.1)Sr2ca2cu3o10

Effect of Heat Treatment on the Superconductivity of Pb-Doped Bi-2212 System: Evidence for a Possible Phase Segregation

SUPERCONDUCTIVITY EVOLUTION OF Bi2201 PHASE UNDER VARIOUS ANNEALING CONDITIONS

The Effect of Constituent Content on Superconductivity and Phase in BiPbSbSrCaCuO System

Superconductivity and Phases of Leaded Bi-Ca-Sr-Cu-O System

Effect of Synthesis Condition on Superconducting Transmission Temperature in Tl-Ba-Ca-Cu-O System

Effect of Oxygen Stoichiometry on T(sub C) of Bi-based Superconductors

Study on Phase-Formation Mechanism and Intergrowth for Bi(Pb)-Sr-Ca-Cu-O System

Preparation and Superconductivity of Bi3PbCa3Sr3Cu4Oy

Effect of Annealing on the Superconductivity Ofbi2sr2

Influence of Oxygen-Content on Superconductivity of Bi-System Material

Charge-transfer induced by Pb-doping and annealing in Bi-2212 phase superconductor