Abstract:The polymerization of styrene (St) with a modified rare earth catalyst system composed of neodymium tricarboxylate (Nd), triisobutyl aluminium (Al) and n-butyl chloride (BCL) was carried out in cyclohexane. The effects of preparation procedure of the catalyst system (the molar ratios of Al/Nd and of BCL/Nd, ageing temperature and ageing time) and reaction conditions (catalyst concentration, polymerization temperature and polymerization time) on St polymerization, catalytic activity, molecular weight and molecular weight distribution of the resultant polymers were investigated. The catalytic activity depended mainly on the molar ratios of Al/Nd and BCL/Nd, the catalyst concentration, the polymerization temperature and time. High molecular weight. of polystyrene could be obtained with the catalyst with low Al/Nd and BCL/Nd ratios aged at relatively low temperature for relatively short time. The molecular weight of polymers increased with a decrease in polymerization temperature. The optimum conditions for obtaining high molecular weight polystyrene are as follows: Al/Nd = 8 similar to 12 (molar ratio), BCL/Nd = 5 similar to 25 (molar ratio), T = 40 similar to 50 degrees C, t(a) = 6 similar to 20 h, Nd/St = 1.5 x 10(-4) similar to 6.0 x 10(-4) ( molar ratio), TP = 40 similar to 50 degrees C. The molecular weight of the polymers reached high weight-average (M) values (M-W = 7.6 x 10(5) g mol(-1)) when Al/Nd = 10. The molecular weight decreased and molecular weight distribution became broad when excess Al or BCL existed in the catalyst system. The polymer obtained was extracted by 2-butanone and then separated into an insoluble fraction and a soluble fraction. The DSC characterization of the insoluble fraction shows that its melting point is around 268 degrees C, which indicating that the insoluble fraction mainly contains syndiotactic polystyrene. It is shown from polarized optical micrograph that the soluble fraction also contains some segments with high stereoregularity.

Stereospecific Polymerization of Styrene Using A Homogeneous Lanthanide Catalyst

Kinetics and Mechanism of Bulk Polymerization of Styrene Catalyzed by Rare Earth Catalyst

Styrene polymerization with ternary neodymium-based catalyst system: effects of catalyst preparation procedures

Polymerization of Styrene Catalyzed by ((PNP)-N-Lambda-P-Lambda) Cobalt(II) Complexes/Ethylaluminum Sesquichloride

Full‐range Kinetic Study on Bulk Syndiotactic Polymerization of Styrene with Homogeneous Metallocene Catalysis

Synthesis Of Powdery Syndiotactic Polystyrene With Homogeneous Metallocene Catalysts - Kinetics And Morphologies

STUDIES ON BULK SYNDIOTACTIC POLYMERIZATION OF STYRENE CATALYZED BY METALLOCENE

Stereospecific Polymerization of 1,3-Butadiene Catalyzed by Cobalt Complexes Bearing N-containing Diphosphine PNP Ligands

Highly Selective Synthesis Of Co2 Copolymer From Styrene Oxide

Stereospecific Polymerization of 1,3-Butadiene Catalyzed by [NNO] Cobalt Complexes

Polymerization of Styrene by Rare Earth Coordination Catalystst

Polymerization of Styrene by Novel Ni(Ii)- and Pd(Ii)-Based Complexes

Styrene Polymerization with Rare Earth Catalysts Using a Magnesium Alkyl Cocatalyst

Homopolymerization and Copolymerization of Isoprene and Styrene with A Neodymium Catalyst Using an Alkylmagnesium Cocatalyst

Copolymerization of Butadiene and Styrene with Neodymium Naphthenate Based Catalyst

SYNTHESIS OF HIGH MOLECULAR WEIGHT POLYSTYRENE WITH A RARE EARTH CATALYST

New Neutral Ni(II)- and Pd(II)-based Initiators for Polymerization of Styrene

N-Octyloxyallene Homopolymerization and Random Copolymerization with Styrene Using Catalyst System Composed of Lanthanide Schiff-base Complexes and Al(i-Bu)3

Homogeneous rare earth coordination catalysts for copolymerization of styrene with acrylonitrile

Polymerization of Styrene Catalyzed by Rare Earth Schiff Base Complexes

A Novel Catalytic System-Ndcl3 Center Dot Hmpa/Al(I-Bu)(3) for Copolymerization of Isoprene and Styrene