Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Hydrothermal Preparation of Zn_3(OH)_2V_2O_7·2H_2O Nanodisks

Hydrothermal Preparation of Zn-3(OH)(2)V2O7 center dot 2H(2)O Nanodisks

Self-assembled Flower-Like Hierarchical Spheres and Nanobelts of Manganese Oxide by Hydrothermal Method and Morphology Control of Them

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Synthesis of cadmium hydroxide nanoflake and nanowisker by hydrothermal method

Uniform single-crystalline zinc oxide round nanodisks, a comprehensive study on the hydrothermal growth

Hydrothermal Preparation and Characterization of MnWO4Nanowires

Hexagonal Nanodisks of Cadmium Hydroxide and Oxide with Nanoporous Structure

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Crystallized Zn3(OH)2V2O7·nH2O: Hydrothermal Synthesis and Magnetic Property

Hydrothermal synthesis of novel Zn2SnO4 octahedron microstructures assembled with hexagon nanoplates

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Hydrothermal Preparation of ZnO Nanorods Using Zinc Powder As Precursor and Their Characterization

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

Growth Of Zno Crystals With Branched Spindles And Prismatic Whiskers From Zn-3(Oh)(2)V2o7 Center Dot H2o Nanosheets By A Hydrothermal Route

Shape Evolution Of Pb (Zr,Ti)O-3 Nanocrystals Under Hydrothermal Conditions

Preparation of dispersive zinc oxide nano-particles via hydrothermal modification route

PEG Assisted Hydrothermal Synthesis of ZnO Nanorods

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

Synthesis of Cup-Like ZnO Microcrystals Via a CTAB-assisted Hydrothermal Route