Abstract:The presence of oxide layers covering the surface of aluminum is known to impede the hydrogen production reaction. These oxide layers can be broken by adding catalysts and increasing the aluminum-water reaction temperature. Common catalysts used are alkaline catalysts that are capable of achieving high hydrogen production rates in a short time at lower temperatures, while intermediate temperatures of above 50 °C can accelerate the hydration reaction of the oxide layer. Herein, the mixture of NaOH and NaAlO2 catalysts was employed to attain a stable NaAlO2 solution and continuous reaction of NaOH and aluminum. This research analyzes the influence of temperature between 32 and 80 °C on the aluminum, 0.3 M NaOH and 0.001 M NaAlO2 catalysts solution at atmospheric pressure. All solutions produces a similar hydrogen yields and rate. Solutions containing NaAlO2 indicate reverse reaction that surpressing the Al(OH)3 precipitation. Residue from the reaction is investigated using X-ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), and Scanning Electron Microscope (SEM). The volume of hydrogen produced is evaluated using a mathematical mass reduction and shrinking core model. The rate of hydrogen production depends largely on the aqueous solution's temperature, with an activation energy of 47.4 kJ/mol. Based on the findings, it is readily apparent that the reaction only produced gibbsite and bayerite, with gibbsite and bayerite being dominant at 32–70 °C and 80 °C, respectively. The mass reduction model fits well with the present results with only an average 5.1 mL deviation, whereas the shrinking core model generally tends to result in underestimated values with an average deviation of 23.9 mL. Copyright © 2023 by Authors, Published by BCREC Group. This is an open access article under the CC BY-SA License (https://creativecommons.org/licenses/by-sa/4.0).

Study of Hydrogen Production from Al-NaOH and Application of Its By-Product

Study of hydrogen generation from the hydrolysis of aluminum in NaOH solution

Molten Salt-Enhanced Production of Hydrogen by Using Skimmed Hot Dross from Aluminum Remelting at High Temperature

Kinetic Study of the Aluminum–water Reaction Using NaOH/NaAlO2 Catalyst for Hydrogen Production from Aluminum Cans Waste

Materials to Generate Hydrogen Continuously by Aluminium and Water Reaction at Room Temperature and Normal Pressure

Aluminum Hydrolysis for Hydrogen Generation Enhanced by Sodium Hydride

Portable Water-Using H-2 Production Materials Converted From Waste Aluminum

Improved Hydrogen Generation from the Hydrolysis of Aluminum Ball Milled with Hydride

Study on Hydrogen Generation from the Hydrolysis of a Ball Milled Aluminum/calcium Hydride Composite

Hydrogen production by water splitting using commercial Al pellets in a circulating NaOH flow reactor

Experimental Researches on Hydrogen Generation by Aluminum with Adding Lithium at High Temperature

Combined Usage of Sodium Borohydride and Aluminum Powder for High‐performance Hydrogen Generation

Hydrolysis-Based Hydrogen Generation Investigation of Aluminum System Adding Low-Melting Metals

Investigation on the Improved Hydrolysis of Aluminum–calcium Hydride-Salt Mixture Elaborated by Ball Milling

Study of the Controllable Reactivity of Aluminum Alloys and Their Promising Application for Hydrogen Generation

Thermogravimetric Analysis of Hydrogen Production of Al–Mg–Li Particles and Water

Controlled and Safe Hydrogen Generation from Waste Aluminum and Water, a New Approach to Hydrogen Generation

Experimental Study on Catalyst-Free High-Temperature and High-Pressure Aluminum-Water Reaction Characteristics Using Metal As Energy Carrier

The Superior Hydrogen-Generation Performance of Multi-Component Al Alloys by the Hydrolysis Reaction

Metal Substrate Enhanced Hydrogen Production of Aluminum Fed Liquid Phase Ga–In Alloy Inside Aqueous Solution

Experimental Study on the Effect of Low Melting Point Metal Additives on Hydrogen Production in the Aluminum–water Reaction