Abstract:To refine the microstructure and form Ti3Al2 and C14 nano particles, and then improve strength and strain simultaneously, the Ti48Al2Cr2Nb 2.5 C alloy has been prepared under ultrasonic wave. Size of lamellar colony, lamellar spacing, phase composition, compressive properties and the related mechanisms have been studied. Results show that size of lamellar colony decreases from 40.7 to 33.0 mu m and lamellar spacing decreases from 1.5 to 0.8 mu m. Average length-diameter ratio of Ti2AlC decreases from 5.4 to 1.9 with increasing the ultrasonic treatment time from 20 to 100 s. Two kinds of nanoparticles form. One is hexagonal Ti3Al2 phase, which has incoherent relationship with gamma phase. Another is Ti(Al, Cr)2 phase with C14 structure. The Ti2AlC and alpha grain are refined by undercooling nucleation and dendrite fragmentation in solid-liquid two-phase area. The active dislocations and vacancy under ultrasonic promote the diffusion of Ti and Cr, and then induce the Ti3Al2 and Ti(Al, Cr)2 formed during solid-phase transformation. Compressive results show that the strength increases from 1901 to 2532 MPa, and the strain simultaneously increases from 27 to 34% with increasing the time from 0 to 100 s. The lattice distortion caused by the difference in thermal expansion coefficient between the Ti3Al2, Ti(Al, Cr)2 and matrix and the microstructure refined by ultrasonic jointly hinder dislocation slip to strengthen the alloy. The refinement and uniform distribution of Ti2AlC hinder crack propagation to improve toughness.

Effect of High Density Ultrasonic on the Microstructure and Refining Property of Al–5Ti–0.25C Grain Refiner Alloy

Effect of high intensitive ultrasound on AlTiC refiner

Research on Microstructure and Refining Performance of Al-Ti-C Grain Refiner Prepared by Ultrasonic Coupling

Effect of ultrasonic field on undercooling nucleation of TiC particles in AlTiC refiner

Research on Synthesizing Process under Ultrasound Coupling and Refining Performance of Al-Ti-C Grain Refiner

Coupling Effect of Adding Al-Ti-C Grain Refiner and Introducing Ultrasound to Molten Melt on the Microstructure of 7050 Aluminum Alloy

Influence of high-intensity ultrasound on grain refining performance of Al–5Ti–1B master alloy on aluminium

A Novel Method for Grain Refinement and Microstructure Modification in Tial Alloy by Ultrasonic Vibration

Austenite Grain Refinement and Subsequent Martensite Transformation of Ternary Cu–Al–Ni Alloy Solidified Within Ultrasonic Field

Effect of High-intensity Ultrasonic on the Microstructure and Grain Refinement of Al-5Ti-1B Master Alloy

Microstructure and Properties of As-Cast Al-4.5Cu-1.5Mg Alloy Refined with Ti-supported TiC Nanoparticles Via Ultrasonic-Assisted Addition

A Novel Method and Mechanism for Simultaneously Refining Microstructure and Controlling Grain Orientation in Ti48Al2Cr2Nb2.5C Alloy

Grain Refinement of Al-5Ti-0.62C-0.2Nd Grain Refiner for Commercial Pure Aluminum and Its Effect on Mechanical Properties

Effect of Al-5Ti-0.2C Refiner on Microstructure and Mechanical Properties of 5356 Aluminum Alloy

Microstructure Modification and Mechanical Performances Enhancement of Ti44Al6Nb1Cr Alloy by Ultrasound Treatment

Effect of Al-TiO2-C-XY2O3 Refiner on Grain Size and Mechanical Properties of Al-5Cu Alloy

Experimental study of grain refinement by ultrasonic treatment during continuous casting

Effects of Al-Ti-C Refiner and Forming Processes on the Microstructure and Properties of Al-Zn-Mg-Cu Alloys

Effect of ultrasonic melt processing and Al-Ti-B on the microstructural refinement of recycled Al alloys

Induced Formation of Nano Precipitates and Improve Microstructure and Mechanical Properties by Ultrasonic Wave in the Solid-Liquid Two-Phase Area of As-Cast Ti48Al2Cr2Nb 2.5 C Alloy

EFFECT OF HIGH-INTENSITY ULTRASONIC TREATMENT ON REFINEMENT OF Al-5Cu ALLOY INGOTS