In situ FTIR studies of coadsorption of CN− and CO on Pt(110) electrode surface
li tian,juntao li,李君涛,jinyu ye,chunhua zhen,甄春花,shigang sun,孙世刚
DOI: https://doi.org/10.1016/j.jelechem.2011.04.028
IF: 4.598
2011-01-01
Journal of Electroanalytical Chemistry
Abstract:Highlights ► CN − and CO coadsorption on Pt(1 1 0) was studied by in situ FTIR spectroscopy for the first time, and important results were reported. ► It has demonstrated that CN − ad has an inhibition effect for CO ad oxidation, while the anodic stripping of CO ad do not affect on previously adsorbed CN − . ► The results revealed the strong interaction between CN − ad and CO ad at Pt(1 1 0) surface in the coadsorption system. Abstract The coadsorption of CN − and CO on Pt(1 1 0) electrode in acid solutions was investigated by using cyclic voltammetry and in situ FTIR spectroscopy. In comparison with individual adsorption of CO or CN − , the onset oxidation potential of CO (CO ad ) coadsorbed with CN − is positively shifted ca. 100 mV, and its oxidation peak is postponed ca. 260 mV together with a significant decrease in current density. When the coadsorbed CO has been stripped completely, the CV recovers the feature of Pt(1 1 0)/CN − surface, which signifies that the coadsorption of CO does not affect the oxidation behavior of the coadsorbed CN − ( CN ad - ). In comparison of CN − and CO adsorbed alone, the CN ad - band is blue shifted from 2090 to 2108 cm −1 at 0.0 V, and the stark tuning rate is decreased dramatically from 53 to 4 cm −1 V −1 ; while the CO ad band is red shifted from 2075 to 2064 cm −1 at 0.0 V, and the stark tuning rate is slightly decreased from 24 to 19 cm −1 V −1 , The result revealed the strong interaction between CN ad - and CO ad at Pt(1 1 0) surface in the coadsorption system. Keywords Pt(1 1 0) Cyanide Carbon monoxide Coadsorption In situ FTIR spectroscopy 1 Introduction Molecular coadsorption is a common and important interfacial phenomenon in electrocatalytic processes. Studying the effect and nature of the intermolecular interactions involved in the coadsorption is of particularly significance in fundamental of electrocatalysis and other relevant fields, because of its distinct effect on adsorbate structure and reactivity at the metal–solution interface [1] . Much research has been reported on CO and CN − coadsorption system on poly- and single crystal Pt electrode by using cyclic voltammetry and in situ FTIR spectroscopy [2–8] . The significances consist in (1) The structure of CO and CN − is relatively simple, and they are often used to study the interactions involved in coadsorption system and dynamics of the interface as model molecules; (2) CO is a poison/reaction intermediate in electrocatalytic oxidation of organic fuel molecules, and study the relationship between reactivity of adsorbed CO and surface structure of the catalyst provides the opportunity to design new CO tolerant catalyst [9] ; (3) CN − is a important reaction intermediate in many important electrocatalytic reactions, for example, amino acid can be dissociated into CN − adsorbate on Pt, Au and other transition metal surfaces [10,11] . Moreover, CN − is widely applied in pharmaceutical chemistry and chemical industry, such as gold recovery, electroplating. [12] ; (4) both CO and CN − have strong interaction with Pt, are therefore often employed as probe molecules to characterize the surface structure of Pt, surface bonding and local electrostatic environment [13,14] . The single crystal electrodes have a well-defined atomic arrangement. As a consequence, the investigation of coadsorption of CO and CN − on single crystal electrode at a molecular lever is of significance in understanding catalytic mechanism and adsorption process, as well as probing the nature of surface and interface. During the past years, however, most efforts have focused only on the coadsorption of CN − and CO on Pt(1 1 1) surface [2–5] , mainly due to that a stable coadsorption of CN − and CO system could be formed on the Pt(1 1 1) electrode. The studies of coadsorption of CN − and CO on other platinum single crystal planes is quite limited, such as Pt(1 1 0) and Pt(1 0 0), since the coadsorption on such surfaces is relatively complex and unstable. Electrochemical in situ infrared spectroscopy can give information about chemical nature of adsorbates, surface bonding and orientation at molecular level [15] . In current studies, the coadsorption and oxidation of CO and CN − , as well as the individual adsorption of CO or CN − on a Pt(1 1 0) single crystal electrode were investigated by using used cyclic voltammetry and in situ FTIR spectroscopy. New insight has been achieved upon revealing the interaction of coadsorbed CO and CN − on the Pt(1 1 0) electrode. 2 Experimental Pt(1 1 0) single crystal electrode applied in cyclic voltammetry studies is a bead-type about 2 mm in diameter. The Pt(1 1 0) electrode for the in situ FTIR spectroscopy studies is a disk of ca. 10 mm in diameter. Both Pt(1 1 0) single crystal electrodes were treated before each measurement using Clavilier’s methods [16] , i.e. they were annealed in hydrogen–oxygen flame first, and then quenched with ultrapure water (Milli-Q 18.2 MΩ cm) after having been cooled in the air, immersed finally in a 0.1 M NaCN (>95%, A.R., China medical company) solution for approximately 3 min to form a saturated CN − adlayer (dented thereafter Pt(1 1 0)/CN − ). The Pt(1 1 0)/CN − was subsequently rinsed and transferred to the electrochemical cell or spectroelectrochemical IR cell containing cyanide-free 0.1 M H 2 SO 4 solution (GR, Shanghai zhenxing) under protection of a droplet of ultrapure water. CO adsorption on Pt(1 1 0) or on the Pt(1 1 0)/CN − were conducted potentiostatically at −0.1 V by blowing CO gas (99.9%, Linde gas) into the electrochemical cell or spectroelectrochemical IR cell. The CO gas flow was stopped until current flowing dropped to zero. CO dissolved in the solution was then removed by bubbling N 2 (99.999%, Linde gas) for ca. 20 min. Cyclic voltammetry were recorded at a sweep rate of 50 mV s −1 . In situ FTIR spectroscopy experiments were carried out on a Nicolet 8700 research FTIR spectrometer (Thermo Scientific) equipped with a nitrogen cooled MCT-A detector using p-polarized light. The spectroelectrochemical IR cell was assembled with a prismatic CaF 2 IR window beveled at 60°. Each spectrum was consisted of 100 interferograms and collected at 8 cm −1 resolution, which took ca. 1.5 min. The Nicolet 8700 FTIR spectrometer was purged throughout the experiment with clean air free of CO 2 and H 2 O provided by a Whatman 74–5041 clean air package. The multi-potential step FTIR spectroscopy (MSFTIRS) procedure [17] was applied to collect in situ FIIR spectra, which were represented as potential-difference spectra calculated using equation bellow (1) Δ R R = R ( E S ) - R ( E R ) R ( E R ) where R ( E S ) and R ( E R ) are single beam spectra recorded at sample potential E S and reference potential E R , respectively. The potentials were measured against a saturated calomel electrode (SCE), and all experiments were carried out at room temperature. 3 Results and discussion 3.1 CO adsorption Before presenting the coadsorption behaviors of CO and CN − , it is necessary to consider the features of CO and CN − adsorbed individually on Pt(1 1 0) in acid media. While much study has been reported about the former adsorbate [18–23] , we describe here briefly the CV features of CO adsorption on Pt(1 1 0) electrode under the present conditions. As shown in Fig. 1 , a sharp anodic peak appears at 0.408 V in the cyclic voltammogram of Pt(1 1 0) covered with a saturation layer of adsorbed CO (Pt(1 1 0)/CO) in 0.1 M H 2 SO 4 , the oxidation charge is measured at 396 μC cm –2 . In comparison with the hydrogen adsorption charge of 220.5 μC cm –2 measured with Pt(1 1 0) in the same 0.1 M H 2 SO 4 solution, the coverage of a saturation layer of CO on Pt(1 1 0) is estimated ca. 0.90, which is good agreement with previously reported results [18] . The onset potential of CO ad oxidation on Pt(1 1 0) is measured ca . 0.1 V from the insert, i.e. the magnified cyclic voltammogram. In situ FTIR spectra of the Pt(1 1 0)/CO in 0.1 M H 2 SO 4 are displayed in Fig. 2 These spectra were recorded on different potentials which are increasing progressively in anodic polarization direction. In Fig. 2 a the spectrum collected at 0.70 V was used as the reference spectrum, which does not contain IR absorption of CO ad since it has been completely removed by oxidation at this potential. As a result, the IR absorption of CO ad at lower potentials will give a negative single band as predicted by the Eq. 1. However, the reference spectrum in Fig. 2 b was chosen that recorded at −0.25 V, at which no CO 2 produced from CO ad oxidation, resulting in also a negative single band of CO 2 . The downward band at 2060 cm −1 in Fig. 2 a is assigned to linear adsorbed CO, while the band at 2343 cm −1 in Fig. 2 b is attributed to IR absorption of solution CO 2 species. Along with increase of electrode potential in the anodic polarization, the frequency of the CO ad band is blue shifted from 2068 cm −1 at −0.25 V to 2078 cm −1 at 0.15 V, then the CO ad band is red shifted and its intensity decreases, signifying the oxidation of CO ad . We can infer that, from the variation of in situ FTIR spectra in Fig. 2 , the CO ad onset oxidation potential is close to 0.10 V where the CO 2 band appears clearly in the spectrum and its intensity is increased above this potential. Such value is in good agreement with the onset oxidation potential measured from the voltammogram presented in the inset of Fig. 1 . 3.2 CN − adsorption The cyclic voltammograms recorded after CN − adsorption in saturation on Pt(1 1 0) (Pt(1 1 0)/CN − ) under open circuit potential condition are shown in Fig. 3 . The CN − modified electrode was immersed at 0.158 V in the test solution of 0.1 M H 2 SO 4 . On the clean Pt(1 1 0) electrode, current peaks at ca. −0.15 V are attributed to hydrogen adsorption–desorption. This sharp hydrogen adsorption–desorption peak is not disappeared completely on the CN − adsorbed Pt(1 1 0) electrode, which suggests that there are still some CN − free Pt surface sites available for CO adsorption, and no obvious anodic or cathodic peaks are observed at potential above 0.0 V. Moreover, the double layer is become larger after CN − absorbed on Pt(1 1 0), which is also observed on Pt(1 1 1) [24] . The inset to Fig. 3 demonstrates that the hydrogen adsorption–desorption current is gradually increased during electrode potential cycling between −0.25 V and 0.10 V due to the desorption of CN ad - from Pt(1 1 0) surface. In situ FTIR spectra as a function of applied electrode potential recorded in 0.1 M H 2 SO 4 solution for a saturation layer of CN − adsorbed on Pt(1 1 0) are shown in Fig. 4 . The spectrum collected at 0.8 V was set as reference spectrum in Fig. 4 a, since at 0.8 V the CN ad - is almost completely oxidized as evidenced in FTIR spectroscopic study. In order to observe the change of CO 2 band intensity more clearly, the spectrum at 0.0 V is also used as the reference spectrum in Fig. 4 b, where the CN ad - does not oxidize to CO 2 at all. There are two negative bands appeared in the spectra, as reported previously [13,25] . The low-energy band at 2094 cm −1 is assigned to linear adsorbed CN − . The frequency of this CN ad - band is blue shifted from 2094 cm −1 at 0.0 V to 2108 cm −1 at 0.7 V. The high-energy band at 2149 cm −1 is attribute to IR absorption of [Pt(CN) 2 ] 2− complex. The potential dependence is not apparent for the [Pt(CN) 2 ] 2− band. The band at 2343 cm −1 appeared starting from 0.25 V is attributed to CO 2 , which demonstrates that the CN ad - begins to be oxidized into CO 2 at this electrode potential. 3.3 CO/CN − coadsorption Fig. 5 compares the cyclic voltammograms of clean Pt(1 1 0), Pt(1 1 0)/CN − , Pt(1 1 0)/CO, and CN − together with CO coadsorbed on Pt(1 1 0) (Pt(1 1 0)/CO + CN − ) recorded in 0.1 M H 2 SO 4 solution. As stated above, the sharp peaks in the low potential region (−0.25 to 0.20 V) on the clean Pt(1 1 0) are due to hydrogen adsorption–desorption, and the broad anodic peak appearing above 0.5 V together with the cathodic peak at 0.46 V are attributed to oxide formation and reduction on Pt(1 1 0) surface, respectively. It can observe that both hydrogen adsorption–desorption and oxide formation–reduction processes are inhibited on Pt(1 1 0)/CO + CN − surface. In comparison with CO adsorbed alone on Pt(1 1 0), the anodic peak of CO ad oxidation is positively shifted about 260 mV from 0.408 V to 0.67 V together with a significant decrease in peak current density on the Pt(1 1 0)/CO + CN − . This CV result indicates that the CO ad oxidation is inhibited in the CO and CN − coadsorption system. After CO ad striping, the cyclic voltammogram becomes identical to that of the Pt(1 1 0)/CN − . It is evident that the CN ad - has an inhibition effect for CO ad oxidation, while the coadsorption of CO and anodic stripping of CO ad do not affect on previously adsorbed CN − . The possibly reasons for this phenomena may be as follows: (1) The CN ad - species occupy a certain amount of surface sites so that the coverage of CO ad decreases, leading to the decrease of CO ad oxidation current; (2) The oxidation of CO ad needs OH − participation. Since both OH − and CN − are negative charged, it exists a repulsive interaction between them, so the process of OH − adsorption on electrode surface is affected by this repulsive interaction [26] . As a result, the CO ad oxidation is shifted to higher electrode potential region. In situ FTIR spectra of coadsorbed CO and CN − on Pt(1 1 0) are shown in Fig. 6 . The spectra of Fig. 6 a were consecutively recorded by increasing potentials from 0.0 V to 0.70 V, and the spectrum collected at 0.80 V was set as reference. The negative band at 2063 cm −1 , 2113 cm −1 and 2151 cm −1 are assigned to CO ad , CN ad - and [Pt(CN) 2 ] 2− , respectively. It can observe from Fig. 6 b that the CO 2 band begins appearing clearly at 0.2 V. In combining with the result of Fig. 5 , it confirms that the CO 2 species are originated from CO ad oxidation. However, the onset potential of CO ad oxidation in this coadsorption system has been postponed for 100 mV in comparison with the CO ad oxidation in CO adsorption alone on Pt(1 1 0) (see Fig. 2 b). Both cyclic voltammetric and in situ FTIR results demonstrate that the CN ad - plays an inhibition role for CO ad oxidation in coadsorption system. It is interesting that the CV features of CN − in the coadsorption system after CO ad striping remains the same as CN − individually adsorbs on Pt(1 1 0). This is also observed in other coadsorption system such as CO coadsorbed with NO [27] , CN − coadsorption with NO [28] on Pt electrodes . In order to gain insights on the interaction of CO and CN − in their coadsorption on Pt(1 1 0) at a molecule level, the in situ FTIR data reported in Figs. 2, 4 and 6 are further analyzed. Fig. 7 compares the variations of CO and CN − band centers versus E S in different adsorption systems. In the CO and CN − coadsorption system, the CN − band center ( Fig. 7 a) is increased slowly at first with increasing potential from 0.0 to 0.2 V, yielding a small stark tuning rate at 4 cm −1 V −1 , and then decreases progressively with further augmenting electrode potentials. It is evident that, in comparison with CN − adsorption alone on Pt(1 1 0) with a large stark tuning rate of 53 cm −1 V −1 , the stark tuning rate of this band is dramatically decreased, while the CN − band center in the coadsorption system is blue shifted. It is interesting to observe opposite effects upon the CO band. The CO band center in the coadsorption system is red shifted. However, the stark tuning rate in the coadsorption system is measured at 19 cm −1 V −1 , which is slightly decreased in comparison with the value of 24 cm −1 V −1 for the CO adsorption alone on Pt(1 1 0). Moreover, all the phenomena discussed above are also appeared in the case of CN − coadsorption with CO on Pt(1 1 1), and the effect in the stretching frequency of CN ad - appeared in the presence of formic acid and methanol in solution too, even though no CO or other adsorbate could be detected under these conditions [2] . The results in Fig. 7 illustrate clearly a strong interaction between CO and CN − coadsorbed on Pt(1 1 0). According to the boding model of CO and CN − on a Pt surface [29] , it may be interpreted that, in the coadsorption system, the negatively charged CN − induces an increase in the d–π∗ back donation between Pt(1 1 0) and CO ad , leading to a red shift of the CO ad band together with a decrease in Stark tuning rate. However, at the same time, the bond between Pt(1 1 0) and CN ad - is weakened, which increases the strength of the C N bond. As a result, the CN − band is blue shifted and its stark tuning rate is dramatically deceased. 4 Conclusions The interaction of CN − and CO coadsorption on Pt(1 1 0) electrode in acid media was investigated by cyclic voltammetry and in situ FTIR spectroscopy. The study revealed that the coadsorption has a significant effect on the oxidation of CN ad - and CO ad , as well as their interaction on the Pt(1 1 0) surface. The CN ad - band is blue shift, while CO ad band is red shift in the coadsorption system. Moreover, the stark tuning rate of CO ad band is slightly from 24 to 19 cm −1 V −1 ; while the CN-1 band is dramatically decreased from 53 to 4 cm −1 V −1 . After CN ad - and CO ad coadsorbed on Pt(1 1 0), the OH − adsorption on the electrode surface is inhibited because of the repulsive interaction between CN ad - and OH - . As a consequence, the onset oxidation potential of CO ad is positively shifted ca. 100 mV, and the anodic peak potential of CO ad oxidation is postponed about 260 mV with a significant decrease in current density. The cyclic voltammetric studies demonstrated that the anodic stripping of CO ad does not affect the previously adsorbed CN ad - at all. The current investigation is of significance in understanding fundamental of electrocatalysis, since the interactions between coadsorption molecules have a distinct effect on adsorbate structure and reactivity at the metal–solution interface. Acknowledgment This study was financially supported by NSFC (Grants 2083305 and 21021002 ). References [1] C. Tang S.Z. Zou M.W. Severson M.J. Weaver J. Phys. Chem. B 102 1998 8546 8556 [2] A. Cuesta M. Escudero B Lanova H. Baltruschat Langmuir 25 2009 6500 6507 [3] F. Huerta E. Moralllón J.L. Vazquez Electrochem. Commun. 4 2002 251 254 [4] Isabel. Morales-Moreno A. Cuesta Claudio. Gutiérrez J. Electroanal. Chem. 560 2003 135 141 [5] B. Geng S.X. Liu J. Cai S.Z. Liang Y.X. Chen J. Phys. Chem. C 113 2009 10326 10328 [6] A. Cuesta J. Am. Chem. Soc. 128 2006 13332 13333 [7] A.F. Carley P.R. Davies M.W. Roberts A.K. Santra K.K. Thomas Surf. Sci. 406 1998 587 591 [8] K. Yoshimi M-B. Song M. Ito Surf. Sci. 368 1996 389 395 [9] K.J.J. Mayrhofer M. Arenz B.B. Blizanac V. Stamenkovic P.N. Ross N.M. Markovic Electrochim. Acta 50 2005 5144 5154 [10] C.H. Zhen S.G. Sun C.J. Fan S.P. Chen B.W. Mao F.Y. Jun Electrochim. Acta 49 2004 1249 1255 [11] F. Huerta E. Moralllón J.L. Vazquez A. Aldaz J. Electroanal. Chem. 475 1999 38 45 [12] F. Huerta C. Mele B. Bozzini E. Moralllón J. Electroanal. Chem. 569 2004 53 60 [13] F.J. Huerta E. Moralllón J.L. Vazquez A. Aldaz Surf. Sci. 396 1998 400 410 [14] M.J. Weaver Appl. Surf. Sci. 67 1993 147 159 [15] Z.Y. Zhou S.G. Sun Electrochim. Acta 50 2005 5163 5171 [16] J. Clavilier D. Armand S.G. Sun M. Petit J. Electroanal. Chem. 205 1986 267 277 [17] W.F. Lin S.G. Sun Electrochim. Acta 41 1996 803 809 [18] S.C. Chang Lam-Wing H. Leung M.J. Weaver J. Phys. Chem. 93 1989 5341 5345 [19] F.J. Vidal-Iglesias J. Solla-Gullón J.M. Campiña E. Herrero A. Aldaz J.M. Feliu Electrochim. Acta 54 2009 4459 4466 [20] S. Yamagishi T. Fujimoto Y. Inada H. Orita J. Phys. Chem. B 109 2005 8899 8908 [21] J.C. Davies B.E. Hayde D.J. Pegg Surf. Sci. 467 2000 118 130 [22] F. Dederichs K.A. Friedrich W. Daum J. Phys. Chem. B 104 2000 6626 6632 [23] H. Kita H. Naohara T. Nakato S. taguchi A. Aramata J. Electroanal. Chem. 386 1995 197 206 [24] F. Huerta E. Morallón J. Vázquez Surf. Sci. 431 1999 577 581 [25] K.A. Friedrich W. Daum C. Klüker D. Knabben U. Stimming H. Ibach Surf. Sci. 335 1995 315 325 [26] D. Strmcnik M. Escudero-Escribano K. Kodama V.R. Stamenkovic1 A. Cuesta N.M. Markovic Nat. Chem. 2 2010 880 885 [27] C. Tang S.Z. Zhou S.C. Chang M.J. Weaver J. Electroanal. Chem. 467 1999 92 104 [28] A. Cuesta M. Escudero Phys. Chem. Chem. Phys. 10 2008 3628 3634 [29] D.S. Kellogg J.E. Pemberton J. Phys. Chem. 91 1987 1120 1126
What problem does this paper attempt to address?
-
Cyclic Voltammetric and in Situ FTIR Spectroscopic Studies of Redox of Nitric Oxide and Carbon Monoxide Coadlayers on Pt Electrode
CHENG Qian,JIANG YanXia,SUN ShiGang
DOI: https://doi.org/10.1360/032010-753
2011-01-01
Abstract:The coadsorption behavior of nitric oxide (NO) and carbon monoxide (CO) on the polycrystalline Pt electrode and the influence of CO on the oxidation-reduction reactions of coadsorbed NO were studied by using cyclic voltammetric (CV) and in situ FTIR spectroscopy in acid media. The results demonstrated that the NO/CO adlayers can be adsorbed on the Pt electrode stably at 0.20 V (vs. SCE). CO existed with linear adsorption state (COL), and NO were coadsorded with both bridged adsorption state (NOB) and linear adsorption state (NOL). Due to the coadsorption of COL, the reduction peak potentials of NO were negatively shifted about 0.024 V, and NOB which should have been not accessible to be oxidized were oxidized at 0.93 V. in situ FTIRS further indicated that NO can replace CO which is pre-adsorbed on the Pt electrode, and it is a competitive adsorption process between NO and CO. Both NO and CO can be converted into environment- friendly species, which are NO3- and CO2 respectively. The quantity of NO3- depends on the adsorption quantity of CO on the Pt electrode.
-
Studies of Oxidation Processes of Adsorbed and Solution CO on Pt(110) Electrode by Cyclic Voltammetry and in Situ FTIRS
TIAN Li,LI Jun-tao,YE Jin-yu,ZHEN Chun-hua,SUN Shi-gang
DOI: https://doi.org/10.13208/j.electrochem.2010.03.006
2010-01-01
Abstract:The oxidation processes of adsorbed CO (COad) and solution phase CO (COsol) on Pt(110) electrode were investigated by cyclic voltammetry and in-situ FTIR spectroscopy. It has revealed that in comparison with COad on Pt(110) in a CO-free solution,the oxidation current peak of COsol in a CO-saturated solution is positively shifted ca. 168 mV,and the peak current density has been increased by 6. 70 times. Linear adsorbed CO (COL) is determined by in-situ FTIR spectroscopy as the main species,which is uniformly distributed on Pt (110) surface. In a CO-free solution,the onset potential of COL is measured by in-situ FTIRS ca. 0. 15 V; the COL band is blue-shifted with the increase of electrode potential in the potential range where COL is stable,yielding a Stark tuning rate 30 cm -1·V -1; when the COL is oxidized at E > 0. 15 V,the COL band is red-shifted at a rate of - 56 cm -1·V -1. In the case of CO-saturated solution,the CO2 band could be appeared in the in-situ FTIR spectrum recorded at - 0. 05 V,demonstrating that the onset potential of COL oxidation is negatively shifted ca. 200 mV in comparison with Pt( 110) in a CO-free solution; the COL band is immediately red-shifted with a rate of - 26. 5 cm -1·V -1 when the potential is above - 0. 05 V.
-
CO Adsorption on Electrode of Pt Nanoparticles Investigated by Cyclic Voltammetry and in Situ FTIR Spectroscopy
Wei Chen,Yanxia Jiang,Shigang Sun
DOI: https://doi.org/10.1360/03tb9027
2003-01-01
Chinese Science Bulletin
Abstract:Pt nanoparticles were prepared by the chemical reduction method. The average diameter of Pt nanoparticles was determined to be 2.5 nm by TEM. The electrochemical properties of Pt nanoparticles were studied by cyclic voltammetry. In comparison with massive Pt, the oxidation current peak of CO adsorbed on Pt nanoparticles is broader. Twin adsorbates of CO on Pt nanoparticles were determined by in situ FTIRS for the first time. It has revealed that the linear and twin-bonded CO can be converted into bridge-bonded CO with the variation of electrode potential. A series of special properties of Pt nanoparticles, such as enhanced IR absorption of CO adsorbates, were also observed.
-
A comparative study of CO adsorption on tetrahexahedral Pt nanocrystals and interrelated Pt single crystal electrodes by using cyclic voltammetry and in situ FTIR spectroscopy.
Hai-Xia Liu,Na Tian,Jin-Yu Ye,Bang-An Lu,Jie Ren,Zhi-Chao Huangfu,Zhi-You Zhou,Shi-Gang Sun
DOI: https://doi.org/10.1039/c4fd00136b
2015-01-01
Faraday Discussions
Abstract:This study focuses on CO adsorption at tetrahexahedral Pt nanocrystals (THH Pt NCs) by using cyclic voltammetry and in situ FTIR spectroscopy. Since the electrochemically prepared THH Pt NCs in this study are enclosed by {730} facets which could be considered by a subfacet configuration of 2{210} + {310}, we have also studied CO adsorption on the interrelated Pt(310) and Pt(210) single crystal electrodes as a comparison. Cyclic voltammetry results demonstrated that CO adsorbs dominantly on the (100) sites of THH Pt NCs at low CO coverage (θ(CO)≤ 0.135), while on both (100) and (110) sites at higher CO coverage. On ordered Pt(310) and Pt(210), i.e. they were flame annealed and then cooled in H(2) + Ar, CO adsorption also illustrates relative priority on (100) sites at low CO coverage; while at high CO coverage or on oxygen-disordered Pt(310) and Pt(210) when they were cooled in air after flame annealing, the adsorption of CO presents a weak preference on (100) sites of Pt(310) and even no preference at all on (100) sites of Pt(210). In situ FTIR spectroscopic studies illustrated that CO adsorption on THH Pt NCs yields anomalous infrared effects (AIREs), which are depicted by the Fano-like IR feature on a dense distribution (60 μm(-2)) and the enhancement of abnormal IR absorption on a sparse distribution (22 μm(-2)) of THH Pt NCs on glassy carbon substrate. Systematic investigation of CO coverage dependence of IR features revealed that, on THH Pt NCs, the IR band center (ν(COL)) of linearly bonded CO (COL) is rapidly shifted to higher wavenumbers along with the increase of CO coverage to 0.184, yielding a fast linear increase rate with a high slope (dν(COL)/dθ(IR)(CO) = 219 cm(-1)); when θ > 0.184, the increase of ν(COL) with θCO slows down and deviates drastically from linearity. In contrast, the ν(COL) on the ordered Pt(310) electrode maintains a linear increase with θ(IR)(CO) for the whole range of θ(IR)(CO) variation, and gives a much smaller increase rate of slope 74.3 cm(-1). The significant differences in CO adsorption behavior on THH Pt NCs and on interrelated Pt single crystal planes demonstrated clearly the unique properties of nanoparticles enclosed by high-index facets.
-
Potential Dependence of Cyanide Adsorption at a Pt Electrode in Acidic Solution: an Electrochemical in Situ Infrared Spectroscopic Study
Shao Xiong Liu,Yong Li Zheng,Jie Xu,Jun Cai,Wen Hua Zhang,Jin Long Yang,Yan Xia Chen
DOI: https://doi.org/10.1021/jp400465h
2013-01-01
The Journal of Physical Chemistry C
Abstract:Cyanide adsorption at the Pt film electrode in 0.1 M HClO4 is examined by electrochemical in situ infrared spectroscopy under attenuated total reflection configuration. N-bound Pt-NC with -N equivalent to C stretching frequency from 2060 to 2135 cm(-1), C-bound Pt-CN with -C equivalent to N stretching frequency between 2140 and 2160 cm(-1), and a trans-(HN = CH) adsorbate with C = N stretching frequency at 1639 cm(-1) are identified; the latter only adsorbs at 0.05 V. The evolution of the spectral features reveal that the initial adsorption state of cyanide is in the form of Pt-NCHad, and then it fast splits into Pt-NC; furthermore, Pt-N C will slowly reorient to Pt-C N at longer adsorption time. The orientation of cyanide adsorbate at the Pt electrode surface is further confirmed by (i) the fact that the Stark slope for the -N C band is ca. 3 times larger than that for -C N and (ii) the spectral behavior of coadsorption of CO onto the presaturated cyanide adlayer: for Pt-N C, coadsorbed CO causes a blue shift in C N stretching frequency without intensity change, whereas for Pt-C N, it only causes an increase in C N band intensity. Dipole-dipole coupling effect, interspace compression, and electronic effect are found to be responsible for potential-dependent spectral behavior with and without coadsorbed CO based on calculations using density functional theory.
-
CoPt Nanoparticles and Their Catalytic Properties in Electrooxidation of CO and CH(3)OH Studied by in Situ FTIRS.
Qing-Song Chen,Shi-Gang Sun,Zhi-You Zhou,Yan-Xin Chen,Shi-Bin Deng
DOI: https://doi.org/10.1039/b802047g
2008-01-01
Abstract:CoPt nanoparticles supported on a glassy carbon electrode (denoted as CoPt/GC) were prepared by galvanic replacement reaction between electrodeposited Co nanoparticles and K(2)PtCl(6) solution. Scanning electron microscope (SEM) and transmission electron microscope (TEM) were both employed to characterize the CoPt nanoparticles. It was shown that the CoPt nanoparticles have irregular shapes and most of them exhibit a core-shell structure with a porous Co core and a shell of Pt tiny particles. The composition of the CoPt nanoparticles was analyzed by energy-dispersive X-ray spectroscopy (EDX), which depicts a Co : Pt ratio of ca. 21 : 79. Studies of cyclic voltammetry (CV) demonstrated that CoPt/GC possesses a much higher catalytic activity towards CO and methanol electrooxidation than a nanoscale Pt thin film electrode. In situ FTIR spectroscopic studies have revealed for the first time, that a CoPt nanoparticles electrode exhibits abnormal IR effects (AIREs) for IR absorption of CO adsorbed on it. In comparison with the IR features of CO adsorbed on a bulk Pt electrode, the direction of the IR bands of CO adsorbed on the CoPt/GC electrode is inverted completely, and the intensity of the IR bands has been enhanced up to 15.4 times. The AIREs is significant in detecting the adsorbed intermediate species involved in electrocatalytic reactions. The results demonstrated a reaction mechanism of CH(3)OH oxidation on CoPt/GC in alkaline solutions through evidencing CO(L), CO(M), HCOO(-), CO(3)(2-), HCO(3)(-) and CO(2) as intermediate and product species by in situ FTIRS.
-
[In Situ FTIR Spectrocopic Studies of CO and CN- Adsorbed on Electrode of Nanometer Thin Film of Palladium in Alkaline Solutions].
SG Sun,LR Cai,ZY Zhou,SP Chen
DOI: https://doi.org/10.3321/j.issn:1000-0593.2000.05.003
2000-01-01
Abstract:The adsorption and coadsorption of CO and CN- on electrode of nanometer thin film of palladium (nm-Pd/GC) was studied by using in situ FTIR spectroscopy. The results demonstrated that the nm-Pd/GC electrode exhibited abnormal infrared effects (AIREs) in alkaline solutions as in acid solutions. The characters of AIREs, i.e., the inversion of the direction of IR band, the augmentation of FWHM and the significant enhancement of IR absorption by adsorbed species were observed in all cases of adsorption and coadsorption of CO and CN-. It has been illustrated that strong interaction is existed between adsorbed CO and CN- on nm-Pd/GC surface. The study has contributed towards understanding the surface processes of chemisorption as well as to reveal the origin of nanometer size-effects of thin film materials.
-
In Situ FTIR Spectroscopic Studies of CO Adsorption on Electrodes of Nanometer-Thin Layer of Pt-Ru and Pt-Pd Surface Alloys
Guoqiang Lu,Lirong Cai,Shigang Sun,Junxiang He
DOI: https://doi.org/10.1007/bf03183565
1999-01-01
Abstract:CO adsorption on nanometer-thin layer of surface alloys of Pt-Ru and Pt-Pd prepared by electrochemical codeposition has been studied usingin situ FTIR spectroscopy. Abnormal infrared effects (AIREs) that consist of the enhancement of IR absorption by adsorbed CO on different surface sites and the inversion of IR band direction have been observed on the thin-layer prepared. The results also demonstrate the considerable significance of Pt-Ru and Pt-Pd surface alloys in electrocatalysis applications.
-
Coadsorbate vibrational interactions within mixed carbon monoxide-nitric oxide adlayers on ordered low-index platinum-group electrodes
Catherine Tang,Shouzhong Zou,Si-Chung Chang,Michael J Weaver
DOI: https://doi.org/10.1016/s0022-0728(98)00421-5
IF: 4.598
1999-06-01
Journal of Electroanalytical Chemistry
Abstract:In-situ infrared reflection-absorption spectra are described for saturated mixed carbon monoxide-nitric oxide adlayers in comparison with CO and NO adsorbed separately on selected ordered Pt-group electrodes in aqueous solution in order to assess the nature of the coadsorbate vibrational interactions and hence the adlayer structure and bonding. Both chemisorbates exhibit pronounced intramolecular vibrational fingerprints (νCO, νNO bands) that are sensitive to the local vibrational environment as well as the surface bonding geometry, enabling a microscopic-level assessment of the coadsorbate interactions in relation to CO and NO coadsorbed with water. The surfaces selected—Ir(110), Ir(111), Pt(100), Pt(111), Rh(100), Rh(111), and Pd(111)—yield near-exclusive molecular (rather than dissociative) NO adsorption, yet exhibit differing coverage-dependent NO, and especially CO, spectral and coordinative properties. Progressive displacement of NO by exposing NO-saturated electrodes to dilute CO solutions yielded chiefly molecularly intermixed CO/NO adlayers. This deduction is most straightforward (and quantitative) on Ir(110) and Ir(111), facilitated by the exclusively atop-like adsorption of CO and NO, as gleaned from the single νCO and νNO band frequencies. Both these features on Ir(110) redshift markedly (by 40–60 cm−1) upon dilution with either the other chemisorbate or with coadsorbed water. Such redshifts, along with the observed suppression of the νNO band intensity in the CO/NO mixtures, arise chiefly from composition-dependent dynamic-dipole coupling within the intermixed dipolar adlayers, and are diagnostic of microscopic coadsorbate structure. Similar νNO redshifts induced by dilution with coadsorbed CO are observed on each of the other surfaces. The composition-dependent analysis is facilitated by the observation of a lone coverage-dependent νNO band, associated probably with multifold NO coordination, in both the absence and presence of coadsorbed CO in most cases. While corresponding effects upon the νCO band frequencies are also observed, the spectra on Pt and Rh surfaces include a pair of νCO bands with frequencies, ca. 1800–1850 and 2000–2070 cm−1, suggestive of bridging and atop-like CO coordination, respectively. On Rh(100), Rh(111), Pt(111) and especially Pt(100), NO coadsorption induces CO ‘bridging’ to ‘atop’ site switching. This is largely consistent with the formation of molecularly intermixed CO/NO adlayers where the strong preference of NO for multifold sites shifts CO molecules into neighboring atop-like configurations. On Pt(111), Rh(111), and Pd(111), however, the νCO spectral fingerprints for the CO/NO adlayers suggest the additional presence of segregated compressed ‘CO-rich’ domains. Comparisons are made also with the behaviour of analogous CO/NO adlayers in ultrahigh vacuum.
chemistry, analytical,electrochemistry
-
An electrochemical in situ surface-enhanced raman spectroscopic study of carbon monoxide chemisorption at a gold core-platinum shell nanoparticle electrode with a flow cell
Pu Zhang,Yan-Xia Chen,Jun Cai,Sangzi Z. Liang,Jian-Feng Li,An Wang,Bin Ren,Zhong-Qun Tian
DOI: https://doi.org/10.1021/jp906697b
2009-01-01
Abstract:The adsorption behavior of a CO adlayer at at Au core-Pt shell (Au@Pt) nanoparticle electrode as a function of CO coverage, partial pressure, and electrolyte composition is examined by electrochemical in situ surface-enhanced Raman spectroscopy (SERS) combined with a thin layer flow cell, which allows time-resolved spectro-electrochemical measurements upon sudden exchange of the electrolyte under potential control. We find (i) a clear decrease (increase) in the Pt-COL (C-O-L) peak frequency and all increase of both hands' intensities With COad Coverage; (ii) a slight increase in the Pt-COL and decrease in the C-O-L Stretching frequencies and an increase in both intensities of the COad-saturated layer when switching from CO-saturated to CO-free Solution; (iii) a clear decrease (up to 50%) of intensities of all of the Pt-CO and C-O bands and the SERS background during the Solution switch from H2SO4 or NaOH to Na2SO4; (iv) a slightly higher C-O-L (lower Pt-COL) peak frequency in H2SO4 than that in Na2SO4 and NaOH. The contributions of different factors such as SERS enhancement, Pt-CO binding strength, CO molecular orientation, and dynamic dipole-dipole Coupling interactions among the COad molecules to the SERS spectral behavior are discussed on the basis of the complementary information of both Pt-CO and C-O stretching vibrations.
-
The Mechanism and Kinetics of Cyanide-Assisted Carbon Monoxide Desorption from Pt Electrodes: an Infrared Spectroscopic Study
Bin Geng,Shaoxiong Liu,Jun Cai,Sangzi Liang,Yanxia Chen
DOI: https://doi.org/10.1021/jp9025688
2009-01-01
Abstract:Using a thin layer flow cell, we examined the dynamic process of COad desorption at a Pt film electrode in contact with cyanide (CN−) containing solution by time-resolved electrochemical in situ infrared spectroscopy with attenuated total reflection configuration under well-defined mass transport. The time-resolved IR spectral features reveal that starting with a COad saturated layer (i) there is an inverse linear relationship between the band intensities of COL and CN− stretching; (ii) the CN−/COad displacement transient exhibits a “volcano” shape with three distinct kinetic regions including a slow ignition period, fast increase, and subsequent decay in the rate; (iii) the CN−/COad displacement rate decreases with electrode potential. The results suggest that COad desorption is directly related to the nucleation of CN−ad islands on the surface. The mechanism of cyanide-assisted COad desorption is discussed.
-
The Mechanism of Room Temperature CO Desorption from Pt Electrode
LIU ShaoXiong,KANG Jing,GENG Bin,TAO Qian,CHEN YanXia
DOI: https://doi.org/10.1360/032010-881
2011-01-01
Abstract:The mechanism and kinetics of CO desorption from Pt electrode has been studied by electrochemical in-situ infrared spectroscopy combined with a flow cell. The results reveal that at room temperature CO ad desorption can only be detected in solutions containing CO or CN - whose adsorption energy at Pt electrode is comparable or higher than that of CO ad , but not in solutions with species like Cl - or sulfate. A reciprocal linear relationship between the IR band intensity of CO ad and CN - ad is observed during the CN - -CO ad displacement process. The activation energy for this process is found to be below 40 kJ/mol from temperature-dependent measurements, which is much smaller than the CO adsorption energy at Pt surface (>60 kJ/mol). The results further supports the adsorption driven desorption mechanism we proposed in our recent study, the detailed mechanism for such processes and the associated energy transfer are discussed.
-
CO adsorption kinetics and adlayer build-up studied by combined ATR-FTIR spectroscopy and on-line DEMS under continuous flow conditions
M. Heinen,Y.X. Chen,Z. Jusys,R.J. Behm
DOI: https://doi.org/10.1016/j.electacta.2007.05.020
IF: 6.6
2007-01-01
Electrochimica Acta
Abstract:Using a novel combined spectro-electrochemical DEMS/ATR-FTIRS technique, the CO adsorption kinetics on a Pt film electrode were studied, performing transient CO adsorption experiments at different constant potentials (0.06–0.6V). CO adsorption rate and COad coverage were determined continuously from the CO consumption measured by on-line differential electrochemical mass spectrometry (DEMS). Simultaneously measured FTIR spectra, recorded in situ in an attenuated total reflection (ATR) configuration, allow a direct correlation of the IR band intensity and frequency with COad surface coverage at different constant potentials. The data show that (i) the CO adsorption kinetics are independent of the adsorption potential up to 0.5V, (ii) a significant potential dependence of the ratio between COL and COM for the same coverage, (iii) in the regime of very high COad coverages there is no proportional relation between COad coverage and COL,M intensity, and (iv) a distinct tendency for COad island formation at Eads<0.2V and>0.4V, most likely due to coadsorption of H-upd at the lower potentials and (bi-)sulfate at higher potentials. Finally, at 0.6V, COad oxidation follows a Langmuir–Hinshelwood mechanism with the highest CO2 formation rate at a relative COad coverage of ∼0.4.
-
CO Adsorption on a Pt(111) Surface Partially Covered with FeOx Nanostructures
Yun Liu,Fan Yang,Yanxiao Ning,Qingfei Liu,Yi Zhang,Hao Chen,Xinhe Bao
DOI: https://doi.org/10.1016/j.jechem.2017.02.006
IF: 13.1
2017-01-01
Journal of Energy Chemistry
Abstract:The adsorption of CO on Pt group metals, as a most fundamental elementary reaction step, has been widely studied in catalysis and electrocatalysis. Particularly, the structures of CO on Pt(111) have been extensively investigated, owing to its importance to both fundamental and applied catalysis. Yet, much less is known regarding CO adsorption on a Pt(111) surface modulated by supported oxide nanostructures, which is of more relevance to technical catalysis. We thus investigated the coverage-dependent adsorption of CO on a Pt(111) surface partially covered by FeOx nanostructures, which has been demonstrated as a remarkable catalyst for low-temperature CO oxidation. We found that, due to its strong chemisorption, the coverage-dependent structure of CO on bare Pt is not influenced by the presence of FeOx. But, oxygen-terminated FeOx nanostructures could modulate the diffusivity of CO at their vicinity, and thus affect the formation of ordered CO superstructures at low temperatures. Using scanning tunneling microscopy (STM), we inspected the diffusivity of CO, followed the phase transitions of CO domains, and resolved the molecular details of the coverage-dependent CO structures. Our results provide a full picture for CO adsorption on a Pt(111) surface modulated by oxide nanostructures and shed lights on the inter-adsorbate interaction on metal surfaces.
-
Investigations of coadsorption of carbon monoxide with S or Bi adatoms at a platinum electrode by in-situ FTIR spectroscopy and quantum chemistry analysis
Wen-Feng Lin,Shi-Gang Sun,Zhao-Wu Tian
DOI: https://doi.org/10.1016/0022-0728(93)02929-C
IF: 4.598
1994-01-01
Journal of Electroanalytical Chemistry
Abstract:The adsorption of CO on a Pt electrode was used as a molecular probe, and the surface properties with respect to the electronic structure of the Pt electrocatalyst during modification by S or Bi adatoms were investigated by a combination of cyclic voltammetry, in-situ Fourier transform IR (FTIR) spectroscopy and cluster model analysis using self-consistent charge discrete variational Xα (SCC-DV-Xα) calculations. It is found that the S adatom decreases the ability of the Pt surface to donate electrons, resulting in weakened CO adsorption and increasing vibrational frequency of the CO band of adsorbed CO molecules. However, the opposite effects were observed in the case of Bi adatoms. The electronic and vibrational properties of the potential dependence of CO adsorbed on a Pt electrode were also studied carefully. The results of quantum chemistry calculations are in good agreement with the experimental results of in-situ FTIR spectroscopy and also reveal the deeper significance of the IR spectroscopy data.
-
Oxidation of CO on a Pt−Fe Alloy Electrode Studied by Surface Enhanced Infrared Reflection−Absorption Spectroscopy
M Watanabe,YM Zhu,H Uchida
DOI: https://doi.org/10.1021/jp993001q
2000-01-01
Abstract:To clarify the CO-tolerant mechanism at Pt-based alloy anode catalysts, surface-enhanced infrared reflection-absorption spectroscopy with the attenuated total reflection technique(ATR-SEIRAS), coupled with CV measurement, was used to observe the oxidation process of adsorbed CO on a typical Pt-Fe (Pt-Fe = 0.27/0.73) alloy. The alloy electrode exhibits a lower saturated coverage of CO.(theta(CO) = 0.55) than that of pure Pt (theta(CO) = 1.0). The dominating linear CO is observed around 2000 cm(-1) when the equilibrium adlayer of CO covers the alloy electrode; however, linear and bridged CO and also GOON were found at the pure Pt electrode at the same CO coverage in the non-steady-state, On the basis of our previous results that a Pt skin is formed during the repetitive potential cycling due to the dissolution of Fe on the alloy surface and the skin exhibits less electronic density in the d band, it can be explained that the lowered linear CO coverage and almost no bridged CO are obtained as the result of the lowered back-donation of d electrons from the Pt skin to adsorbates on the alloy surface. The wavenumber shift of the linear CO stretching to a lower value at the alloy, which is not simply predicted by the lowering of the back-donation of the d electron, is ascribed to the weakening of the C-Pt bond. As a presumable effect of the electronic structure change at the Pt skin, the dissociation-oxidation of adsorbed water as well as a formation of adsorbed HOOH species are clearly observed beyond 0.6 V in the electrolyte solution without CO, which is different from that at the pure Pt electrode. Carbonate species can also be detected around 1300-1450cm(-1), which are possibly produced by the surface-reaction of CO2 with water.
-
The Dynamic Nature of CO Adlayers on Pt(111) Electrodes.
Jie Wei,Reihaneh Amirbeigiarab,Yan-Xia Chen,Sung Sakong,Axel Gross,Olaf M. Magnussen
DOI: https://doi.org/10.1002/anie.201913412
2020-01-01
Angewandte Chemie International Edition
Abstract:AbstractCO adlayers on Pt(111) electrode surfaces are an important electrochemical system and of great relevance to electrocatalysis. The potential‐dependent structure and dynamics of these adlayers are complex and still controversial, especially in the CO pre‐oxidation regime. We here employ in situ high‐speed scanning tunneling microscopy for studying the surface phase behavior in CO‐saturated 0.1 m H2SO4 on the millisecond time scale. At potentials near the onset of CO pre‐oxidation local fluctuations in the (2×2)‐CO adlayer are observed, which increase towards more positive potentials. Above 0.20 V (vs. Ag/AgCl), this leads to an adlayer where COad apparently reside on every top site, but still exhibit a (2×2) superstructure modulation. We interpret this observation as a dynamic effect, caused by a small number of highly mobile point defects in the (2×2)‐CO adlayer. As shown by density functional theory calculations, the CO lattice near such defects relaxes into a local (1×1) arrangement, which can rapidly propagate across the surface. This scenario, where a static (2×2) COad sublattice coexists with a highly dynamic sublattice of partially occupied top sites, explains the pronounced COad surface mobility during electrooxidation.
-
Quantum Chemistry and in Situ FTir Spectroscopy Studies on Potential-Dependent Properties of CO Adsorbed on Pt Electrodes
WF LIN,SG SUN,ZQ TIAN,ZW TIAN
DOI: https://doi.org/10.1016/0013-4686(93)80220-t
IF: 6.6
1993-01-01
Electrochimica Acta
Abstract:The electronic and vibrational properties of CO adsorbed on Pt electrodes at different potentials have been studied, by using methods of self-consistent-charge discrete variational Xα (SCC-DV-Xα) cluster calculations and in situ FTir spectroscopy. Two new models have been developed and verified to be successful: (1) using a “metallic state cluster” to imitate a metal (electrode) surface; and (2) charging the cluster and shifting its Fermi level (ϵf) to simulate, according to the relation of —d ϵfe dE, quantitatively the variation of the electrode potential (E). It is shown that the binding of PtCO is dominated by the electric charge transfer of dπPt ⇒ 2π*CO, while that of σCO ⇒ Pt is less important in this binding. The electron occupancy of the 2π* orbital of COads weakens the CO bond and decreases the vCO. Variation of E mainly influences the charge transfer process of dπPt ⇒ 2π*CO, but hardly influences that of σCO ⇒ Pt. A linear potential-dependence of vCO has been shown and the calculated dvCO/dE = 35.0 cm−1 V−1. All results of calculations coincide with the ir experimental data.
-
Electrochemical <i>In Situ</i> Video-STM Studies of the Phase Transition of CO Adlayers on Pt(111) Electrodes
Jie Wei,Yan-Xia Chen,Olaf M. Magnussen
DOI: https://doi.org/10.1021/acs.jpcc.0c10890
2021-01-01
Abstract:The potential-dependent (2 x 2)-3CO -> (root 19 x root 19)R23.4 degrees-13CO phase transition of CO adlayers on Pt(111) in a 0.1 M H2SO4 electrolyte containing minor amounts of CO was studied on the subsecond time scale by in situ high-speed scanning tunneling microscopy. At a potential of 0.20 V versus Ag/AgCl, the (2 x 2)-3CO phase is converted into an apparent (1 x 1)-CO adlayer. Upon increasing the potential to 0.25 V, this adlayer first transiently exhibits both a local (1 x 1) lattice as well as a (root 19 x root 19)R23.4 degrees superlattice before it is gradually transformed into a static (root 19 x root 19)R23.4 degrees-13CO adlayer with a rotated and expanded adsorbate arrangement. In the transient structure, highly dynamic fluctuations in the adsorbate positions are observed. These results can be rationalized by a microscopic mechanism in which the removal of CO adsorbates leads to highly mobile defects with a local (1 x 1) structure in the (2 x 2)-3CO adlayer. With decreasing CO coverage, a densely packed arrangement of these (1 x 1) clusters with (root 19 x root 19)R23.4 degrees symmetry is formed, which subsequently rearranges gradually into the (root 19 x root 19)R23.4 degrees-13CO adlayer.
-
Surface Enhanced Infrared Absorption Spectroscopic Investigation of CO Electrosorption and Electrooxidation on Pt Nanocrystals
Reyisha Duolikun,Yang Yao-Yue,Cai Wen-Bin
DOI: https://doi.org/10.3866/pku.whxb201412011
2015-01-01
Abstract:Electrochemical attenuated total reflection-surface enhanced infrared absorption spectroscopy (ATRSEIRAS) has been used to investigate the facet-dependent adsorption and oxidation of CO on the {100}preferred Pt nanocrystals (NCs). The cyclic voltammogram for the synthesized and then cleaned Pt NCs in a sulfuric acid solution displayed four pairs of redox peaks. The peaks located at 0.26 and 0.36 V were attributed to interfacial hydrogen electro-adsorption/desorption processes on the shortand long-range Pt{100} domains, respectively. Furthermore, the Pt{100} and Pt{111} domains were estimated to account for 34% and 14% of the active sites on the surfaces of the Pt NCs, respectively, based on Bi and Ge irreversible adsorption methods. Potential-dependent spectral features can be used to differentiate the adsorption and oxidation processes of linearly adsorbed CO (COL) species on the three basic planes of the Pt NCs. COL species on the Pt{110} facets were oxidized preferentially, followed sequentially by those on the Pt{111} and Pt{100} facets. COL on Pt{100} required the highest overpotential for their oxidation.