Abstract:We present the design and synthesis of Ca-rich Ca-Al-O oxides, with Ca(2+)/Al(3+) ratios of 1:1, 3:1, 5:1, and 7:1, which were prepared by hydrothermal decomposition of coprecipitated hydrotalcite-like Ca-Al-CO(3) precursors, for high-temperature CO(2) adsorption at 500-700 degrees C. In situ X-ray diffraction measurements indicate that the coprecipitated, Ca-rich, hydrotalcite-like powders with Ca(2+)/Al(3+) ratios of 5:1 and 7:1 contained Ca(OH)(2) and layered double hydroxide (LDH) phases. Upon annealing, LDH was first destroyed at approximately 200 degrees C to form an amorphous matrix, and then at 450-550 degrees C, the Ca(OH)(2) phase was converted into a CaO matrix with incorporated Al(3+) to form a homogeneous solid solution without a disrupted lattice structure. CaO nanocrystals were grown by thermal treatment of the weakly crystalline Ca-Al-O oxide matrix. Thermogravimetric analysis indicates that a CO(2) adsorption capacity of approximately 51 wt.% can be obtained from Ca-rich Ca-Al-O oxides prepared by calcination of 7:1 Ca-Al-CO(3) LDH phases at 600-700 degrees C. Furthermore, a relatively high CO(2) capture capability can be achieved, even with gas flows containing very low CO(2) concentrations (CO(2)/N(2)=10%). Approximately 95.6% of the initial CO(2) adsorption capacity of the adsorbent is retained after 30 cycles of carbonationcalcination. TEM analysis indicates that carbonation-promoted CaCO(3) formation in the Ca-Al-O oxide matrix at 600 degrees C, but a subsequent desorption in N(2) at 700 degrees C, caused the formation CaO nanocrystals of approximately 10 nm. The CaO nanocrystals are widely distributed in the weakly crystalline Ca-Al-O oxide matrix and are present during the carbonationcalcination cycles. This demonstrates that Ca-Al-O sorbents that developed through the synthesis and calcination of Ca-rich Ca-Al LDH phases are suitable for long-term cyclic operation in severe temperature environments.

Properties of Perovskite-Type Sorbent for High-Temperature Production of Oxygen-Enriched Carbon Dioxide Stream

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Properties of Ca-Base Co2 Sorbent Using Ca(Oh)(2) As Precursor

Properties of a Nano CaO/Al<sub>2</sub>O<sub>3</sub>CO<sub>2</sub>Sorbent

Oxygen Sorption/Desorption Kinetics Of Srco0.8fe0.2o3-Delta Perovskite Adsorbent For High Temperature Air Separation

Oxygen absorption/desorption behaviors of Sr0.72Ca0.28Fe1-xAlxO3-δ perovskite oxygen sorbents for air separation

Oxygen sorption/desorption kinetics of SrCo 0.8 Fe 0.2 O 3−δ perovskite adsorbent for high temperature air separation

Tantalum stabilized SrCoO3-δ perovskite membrane for oxygen separation

Phase Transition Behaviors of Sr0.72Ca0.28Fe1-xNixO3-s Perovskite Oxygen Sorbents in a Fixed Bed Reactor

Development of CaO-based Sorbent Doped with Mineral Rejects–bauxite-Tailings in Cyclic CO2 Capture

Effect of A/B-site substitution on oxygen production performance of strontium cobalt based perovskites for CO2 capture application

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Sr2CeO4 As a Robust High Temperature Sorbent for CO2 Capture with Near 100% Sorbent Conversion Efficiency

Development of Highly Effective CaO@Al2O3 with Hierarchical Architecture CO2 Sorbents Via a Scalable Limited-Space Chemical Vapor Deposition Technique

Development of Sintering-Resistant Cao-Based Sorbent Derived from Eggshells and Bauxite Tailings for Cyclic Co2 Capture

Characteristics of SrCo1-xFexO3-δPerovskite Powders with Improved O2/CO2Production Performance for Oxyfuel Combustion

High-Entropy Fluorite Oxide-Modified CaO-Based Sorbent Pellets for Enhanced High-Temperature CO2 Capture

Ca-rich Ca-Al-oxide, high-temperature-stable sorbents prepared from hydrotalcite precursors: synthesis, characterization, and CO2 capture capacity.

A Temperature Programmed Desorption Investigation on the Interaction of Ba0.5Sr0.5Co0.8Fe0.2O3−δ Perovskite Oxides with CO2 in the Absence and Presence of H2O and O2

Perovskite-Based Phase Transition Sorbents for Sorption-Enhanced Oxidative Steam Reforming of Glycerol

EXPERIMENTAL STUDY OF O_2-CO_2 MIXED STREAM PRODUCTION BASED ON PEROVSKITE