Abstract:The purpose of this study was to evaluate in vitro the effect of a phosphoric acid etchant containing benzalkonium chloride on the dentin/adhesive interface in primary teeth. The teeth had caries lesions involving enamel and dentin, and were stored in a 2% glutaraldehyde solution for 2-4 hours. The teeth were divided into five groups of five teeth each: Group 1: Etching for 15 seconds with a semigel 32% phosphoric acid containing benzalkonium chloride; Group 2: Etching with 35% phosphoric acid for 15 seconds; Group 3: Treated with a 2% benzalkonium chloride in a alcoholic solution; Group 4: Conditioned with a 3% benzalkonium chloride in a alcoholic solution (control group); Group 5: The teeth were untreated (control group). The carious tissue was removed with a carbide bur in high-speed and copious air water spray. The overall dimensions and depths of the cavities were determined by the carious tissue removal. After the caries lesion was removed, the cavity was cleaned with an air-water spray and the dentin was treated according to the specific group. The teeth were then restored with Scotchbond Multi-Purpose Plus (3M, St. Paul, MN) and Z-100 resin-based composite (3M, St. Paul, MN) according to the manufacturer's instructions. After the teeth were restored they were stored in water for 24 hours at room temperature and the restorations polished. After storage the teeth were thermally challenged for 500 cycles in temperatures of 50 C and 550 C and then stored in 100% humidity until the sectioning procedures. The teeth were cut into two sections along the longitudinal axis through the center of the teeth and passed the mesial-distal surfaces through the restoration by using a double-face diamond disc with water coolant. The specimens were ground with 320 up to 600 grit silicon carbide paper and polished with 6 mm and 1 mm diamond paste and 0.25 pm alumina solution. The specimens were etched with 10% citric acid for 1 minute and washed with deionized water. After that, they were deproteinized with 10% NaOCl for 5 seconds. The specimens were dried at room temperature sputter-coated with gold and observed with an SEM for assessment of the morphology of the bonded interface. The interface was observed to determine the presence/absence of hybrid layer formation, resin tags, and gaps. In the groups treated only with benzalkonium chloride solutions, spaces were observed in the resin/dentin interface. Similar findings were observed in the control group, which received no treatment on the dentin before primer application. In these groups neither resin tags or hybrid layer formation was observed. The presence of an amorphous layer, which was unremoved smear layer, was noted. The group treated with 35% phosphoric acid showed a hybrid layer formation (8.15 microns). This layer was linked intimately with the peritubular and intertubular dentin. Tags formation was observed towards the pulp under the hybrid layer. In these specimens the gaps were not observed between the dentin layer and bonding materials. The total removal of the smear layer was observed using 37% phosphoric acid with benzalkonium chloride. A hybrid layer (+/- 7.32 microns) and resin-tags attached to this layer were observed similar to the group in which the 35% phosphoric acid was used. The samples showed total removal of the smear layer and no gaps were observed in the dentin/adhesive interface.

Comparison of dentin decalcification between polycarboxylic acids and phosphoric acid

The influence of caries-affected dentin on bonding effect of deciduous teeth

Effect of phosphoric acid containing polyvinylpyrrolidone as protective etchant for dentin bonding

The effect of different conditioning agents on dentin roughness and collagen structure

Effect of etching agent on dentinal adhesive interface in primary teeth

Comparative evaluation of demineralization of radicular dentin with 17% ethylenediaminetetraacetic acid, 10% citric acid, and MTAD at different time intervals: An in vitro study

Effect of acid etching time and technique on interfacial characteristics of the adhesive-dentin bond using differential staining.

Demineralization effect of EDTA, EGTA, CDTA and citric acid on root dentin: a comparative study

Interfacial Interaction of Tartaric Acid with Hydroxyapatite and Enamel

Selective demineralisation of dentine extrafibrillar minerals—A potential method to eliminate water-wet bonding in the etch-and-rinse technique

Effect of experimental dentin etchants on dentin bond strength, metalloproteinase inhibition, and antibiofilm activity

Effects of Phosphoric Acid Pre-Etching on Chemisorption between Enamel and MDP-Containing Universal Adhesives: Chemical and Morphological Characterization, and Evaluation of Its Potential

Comparison of Resistance of Dentin to Erosive Acid after Application of Fluoride to Teeth

Effect of Phytic Acid Etching and Airborne-Particle Abrasion Treatment on the Resin Bond Strength

Comparative study on the anti-demineralization effect of pinus massoniana bark extract and grape seed extract on human root dentin in vitro

Microhardness and characterization of human dental tissue after application of enzymatic chemical agents: In vitro study

Effects of lactic acid etching on immediate and aged bond strength of resin-dentin bonding interface

Comparative study of the effect of laser irradiation and acid etching surface treatment on bonding of some dental restorative materials To dentin surface

Is it possible for a simultaneous biomodification during acid etching on naturally caries-affected dentin bonding?

The effect of phytic acid on enzymatic degradation of dentin

Evaluation of dentin features in teeth after caries removal by three techniques (chemomechanical, mechanical with a smart bur, and air-abrasion): an in vitro study