Investigation on the Thiomer-based Chitosan Scaffold

LI Zhe,CEN Lian,CUI Lei,CAO Yilin

DOI: https://doi.org/10.3969/j.issn.1673-0364.2007.04.003

2007-01-01

Abstract:Objective To prepare thiolated chitosan scaffold containing functional thiol groups for applications in tissue engineering.Methods Thioglycolic acid(TGA) was introduced on the side chain of chitosan(CS) via the amide bond formation between the COOH groups of TGA and NH2 groups of CS mediated by a carbodiimide.The resulting CS-TGA conjugate was mixed with pristine CS to prepare three dimensional porous CS-TGA/CS scaffolds by freeze drying.The mixing ratio was varied to investigate its effect on the properties of final scaffolds.The elemental analysis was done by X-ray Photoelectron Spectroscopy(XPS) and the microstructure of the scaffold was observed by scanning electron microscopy(SEM).Tensile strength of the scaffolds was also measured.Results The scaffold can reach its maximum tensile strength when the mixing proportion of CS-TGA over CS was 7∶3 among the conditions tested.The freezing temperature of-20 ℃ is beneficial to obtain the scaffold with superior tensile strength,homogeneous morphology as well as the narrow distribution of pore size ranging from 100 μm to 300 μm.Conclusion Both the mixing proportion and freezing temperature affect the microstructure and mechanical property of the prepared scaffold.By optimizing freezing temperatures and mixing proportions,thiomer-based chitosan scaffold bearing functional groups can be obtained with satisfactory mechanical properties and uniform morphology.