The Role of Transition Metals on Chemo‐Mechanical Instabilities in Prussian Blue Analogues For K‐Ion Batteries: The Case Study on KNHCF Versus KMHCF
Zheng Li,Bertan Ozdogru,Batuhan Bal,Mark Bowden,Austin Choi,Yizhi Zhang,Haiyan Wang,Vijayakumar Murugesan,Vilas G. Pol,Ömer Özgür Çapraz
DOI: https://doi.org/10.1002/aenm.202301329
IF: 27.8
2023-07-26
Advanced Energy Materials
Abstract:Ni‐based Prussian Blue Analogues (KNHCF) demonstrate better capacity retention than Mn‐based Prussian Blue Analogues (KMHCF) when cycled under the same conditions. Both electrodes undergo similar mechanical deformations during cycling, however, there is a formation of richer organic compounds in cathode‐electrolyte interface layers on the KMHCF cathode with cycling. Faster capacity fade in KMHCF is attributed to the interfacial instabilities, rather than mechanical deformations. Prussian blue analogues (PBAs) cathodes can host diverse monovalent and multivalent metal ions due to their tunable structure. However, their electrochemical performance suffers from poor cycle life associated with chemo‐mechanical instabilities. This study investigates the driving forces behind chemo‐mechanical instabilities in Ni‐ and Mn‐based PBAs cathodes for K‐ion batteries by combining electrochemical analysis, digital image correlation, and spectroscopy techniques. Capacity retention in Ni‐based PBA is 96% whereas it is 91.5% for Mn‐based PBA after 100 cycles at C/5 rate. During charge, the potassium nickel hexacyanoferrate (KNHCF) electrode experiences a positive strain generation whereas the potassium manganese hexacyanoferrate (KMHCF) electrode undergoes initially positive strain generation followed by a reduction in strains at a higher state of charge. Overall, both cathodes undergo similar reversible electrochemical strains in each charge–discharge cycle. There is ~0.80% irreversible strain generation in both cathodes after 5 cycles. XPS studies indicated richer organic layer compounds in the cathode‐electrolyte interface (CEI) layer formed on KMHCF cathodes compared to the KNHCF ones. Faster capacity fades in Mn‐based PBA, compared to Ni‐based ones, is attributed to the formation of richer organic compounds in CEI layers, rather than mechanical deformations. Understanding the driving forces behind instabilities provides a guideline to develop material‐based strategies for better electrochemical performance.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels