Microstructure and Magnetic Properties of Nickel Nano-crystalline Particles

周丹,刘先松,邱士星,贾道宁,胡峰,王鹏鹏
DOI: https://doi.org/10.3969/j.issn.1001-3830.2010.03.008
2010-01-01
Abstract:Nickel nano-crystalline particle was successfully prepared by microwave polyol-reduction technique. The phase composition,morphology and magnetic properties of the as-synthesized samples were characterized by X-ray diffraction (XRD),filed-emission scanning electronic microscope (FESEM) and vibrating sample magnetometer (VSM). The results showed that when the reaction temperature was 120-130℃ and reaction time was more than 2h,the nickel nano-crystalline was obtained with a face-centered cubic structure and an average size of about 100-150nm; when reaction time was 4h,nickel nano-crystalline particle was obtained with coercivity Hc of 14.818kA/m and the saturation magnetization σs of 45.20 A.m2/kg.