Abstract:Combined structure of anodic TiO2 nanotubes and TiO2 nanoparticles (TiNTs-TiNPs) has been synthesized by a facile combination of hydrothermal and chemical vapor deposition methods. Ordered TiO2 nanotubes with smooth walls were fabricated by two step anodization method in ethylene glycol containing NH4F at 50 V. This nanotubular array after annealing at 450 °C was subjected to the hydrothermally produced gaseous environment in an autoclave with diluted TiCl4 solution at its bottom. Vapors of TiCl4 were allowed to react chemically with water vapors for predefined time durations at 180 °C that resulted in the deposition of TiO2 nanoparticles on tubes’ surface and side walls. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) confirmed that for one hour reaction duration, nanoparticles were evenly coated on the walls of nanotubes, whereas, longer durations tend to deteriorate the tubular structure. Consequently, the ordered TiNTs-TiNPs array produced after one hour coating has shown better performance for dye-sensitized solar cell DSSC) in back illumination mode with 130% increase in efficiency as compared to the device based on bare TiO2 nanotubes. The same photoanode has higher reflective properties with higher scattering ability. The solar cell based on this photoanode exhibits higher external quantum efficiency and effective charge transport properties. This study shows that porous ordered 1D structures based on TiO2 are of crucial importance for the high performance of DSSCs.

High-density NiTiO3/TiO2 Nanotubes Synthesized Through Sol–gel Method Using Well-Ordered TiO2 Membranes As Template

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Anodization Fabrication of Highly Ordered Tio2 Nanotubes

Template-based Synthesis and Micro-structure Characterization of TiO2 Nano-array

Fabrication of Double-Walled TiO2 Nanotubes with Bamboo Morphology Via One-Step Alternating Voltage Anodization

Template Assisted Fabrication of TiO<sub>2</sub> and BaTiO<sub>3</sub> Nanotubes

Morphology of TiO_2 Nanotube Arrays Prepared by Anodic Oxidation

Highly Ordered TiO2 Nanotube Arrays with Engineered Electrochemical Energy Storage Performances

Highly ordered combined structure of anodic TiO2 nanotubes and TiO2 nanoparticles prepared by a novel route for dye-sensitized solar cells

Fabrication of free standing anodic titanium oxide membranes with clean surface using recycling process

Synthesis of TiO<sub>2</sub> Nanotube Arrays Through Multistep Anodization

Template Assisted Fabrication of TiO2 and BaTiO3 Nanotubes

Metal Nanoparticle Chains Embedded in TiO2 Nanotubes Prepared by One-Step Electrodeposition

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

Electrochemically Induced Sol-Gel Preparation of Single-Crystalline Tio2 Nanowires

An Electrokinetic Route to Rapid Synthesis of Nickel Hydroxide and Nickel Oxide Nanotubes.

In Situ Template Synthesis of TiO<sub>2</sub> Nanotube Array Films

Fabrication of Self-Branched TiO2 Nanotubes by Anodization Method, Ordering and Crystallinity

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Fabrication of multi-sectional TiO 2 nanotube arrays by anodization

In-situ template synthesis of TiO2 nanotube array films