Synthesis, molecular structure and photovoltaic performance for polythiophenes with β-carboxylate side chains
Jiabin Zhang,Lingpeng Yan,Hongwei Tan,Xiaochen Liu,Yi Lin,Lianping Zhang,Hongyu Wang,Chang-Qi Ma
DOI: https://doi.org/10.1007/s10965-021-02546-6
IF: 3.061
2021-04-27
Journal of Polymer Research
Abstract:To lower the HOMO energy level of polythiophenes, carboxylate groups were introduced to the β-position of the thiophene unit, by which two polythiophenes with tetrathiophene (poly[5,5′′-(bis-3,3′′-((2-butyloctyl)-carboxylate)-2,2′:2′,2′′-terthiophene)-<i>alt</i>-5-thiophene], <b>P-4T-2COOR</b>) or pentathiophene (poly[5,5′′-(bis-3,3′′-((2-butyloctyl)-carboxylate)-2,2′:2′,2′′-terthiophene)-<i>alt</i>-5,5′-(2,2′-bithiophene)], <b>P-5T-2COOR</b>) repeating unit were synthesized. Absorption spectroscopy and cyclic voltammetry measurements revealed that the β-carboxylate substitution red-shifts the maximum absorption wavelength (<i>λ</i><sub>max</sub><sup>abs</sup>) in solution owing to the electron accepting nature of the carboxylate group. In addition, the introduction of β-carboxylate reduces the HOMO level from -5.09 eV for <b>P3HT</b> to -5.34 eV and -5.18 eV for <b>P-4T-2COOR</b> and <b>P-5T-2COOR</b>, respectively, which is in good agreement with quantum chemisty calculation results. However, the β-carboxylate side chain showed different orientation to that of P3HT, which leads to weaker intermolecular π-π interaction as confirmed by less red-shited absorption in thin solid film and the quantum calculation results. Polymer solar cells using <b>P-4T-2COOR</b> and <b>P-5T-2COOR</b> as the electron donor, 3,9‐bis(2‐methylene‐(3‐(1,1‐dicyanomethylene)‐indanone))‐5,5,11,11‐tetrakis(4‐hexylphenyl)‐dithieno[2,3‐<i>d</i>:2′,3′‐<i>d</i>′]‐s‐indaceno‐[1,2‐<i>b</i>:5,6-<i>b</i>′]di‐thiophene (ITIC) as the electron acceptor were fabricated and tested. The <b>P-4T-2COOR</b> and <b>P-5T-2COOR</b> based cells showed high open circuit (<i>V</i><sub>OC</sub>) of 0.73–0.99 V, significantly higher than that of <b>P3HT</b> based cell (<i>V</i><sub>OC</sub> of 0.52 V), which can be ascribed to the lower HOMO energy levels and less condensed molecular packing of these two polymers.
polymer science