Abstract:Titanium and its alloys have superior electrochemical properties compared to other alloy systems due to the formation of a protective TiO2 film on metal surfaces. The ability to generate the protective oxide layer will depend upon the type of alloy to be used. The aim of this work was to characterize the electrochemical corrosion behavior of titanium Ti-CP2 and alloys Ti-6Al-2Sn-4Zr-2Mo, Ti-6Al-4V, and Ti Beta-C. Samples were anodized in 1 M H2SO4 and H3PO4 solutions with a current density of 0.025 A/cm2. Electrochemical tests on anodized alloys were carried out using a three-electrode cell and exposed in two electrolytes, i.e., 3.5 wt % NaCl and 3.5 wt % H2SO4 solutions at room temperature. Scanning electron microscopy (SEM) was used to observe the morphology of anodized surfaces. The electrochemical techniques used were cyclic potentiodynamic polarization (CPP) and electrochemical noise (EN), based on the ASTM-G61 and G199 standards. Regarding EN, two methods of data analysis were used: the frequency domain (power spectral density, PSD) and time-frequency domain (discrete wavelet transform). For non-anodized alloys, the results by CCP and EN indicate icorr values of ×10−6 A/cm2. However, under anodizing conditions, the icorr values vary from ×10−7 to ×10−9 A/cm2. The PSD Ψ0 values are higher for non-anodized alloys, while in anodized conditions, the values range from −138/−122 dBi (A2·Hz−1)1/2 to −131/−180 dBi (A2·Hz−1)1/2. Furthermore, the results indicated that the alloys anodized in the H3PO4 bath showed an electrochemical behavior that can be associated with a more homogeneous passive layer when exposed to the 3.5 wt % NaCl electrolyte. Alloys containing more beta-phase stabilizers formed a less homogeneous anodized layer. These alloys are widely used in aeronautical applications; thus, it is essential that these alloys have excellent corrosion performance in chloride and acid rain environments.

[Study of Corrosion Behavior of Titanium with Anodized Oxidation Film].

[Corrosion Resistant Properties of Different Anodized Microtopographies on Titanium Surfaces].

Electrochemical Corrosion Behaviors of Titanium Covered by Various TiO2 Nanotube Films in Artificial Saliva

Studies on the Corrosion Resistance of Multicolor Anodic Titanium Oxide Films

Corrosion Behaviors of TiO 2 Nanotube Layers on Titanium in Hank's Solution

Corrosion Behaviour of the Anodic Oxide Film on Commercially Pure Titanium in NaCl Environment

Anti-Corrosion Property of Atomic Layer Deposition Films for Anodized Aluminum

Electrochemical Corrosion of Titanium and Titanium Alloys Anodized in H2SO4 and H3PO4 Solutions

The Corrosion Resistance of Titanium after Micro Arc Oxidation Treatment

Corrosion resistance research on pure titanium with different roughness of the surface

Surface characteristics and electrochemical corrosion behavior of a pre-anodized microarc oxidation coating on titanium alloy.

Oxidation resistance and corrosion behavior of hot-dip aluminized coatings on commercial-purity titanium

Influence of Incremental Rate of Anodising Current on Roughness and Electrochemical Corrosion of Oxide Film on Titanium Alloy Ti–10V–2Fe–3Al

Effect of Anodization Time on Morphology and Electrochemical Impedance of Andic Oxide Films on Titanium Alloy in Tartrate Solution

In Vitro Corrosion Study of Different TiO2 Nanotube Layers on Titanium in Solution with Serum Proteins

Electrochemical anodizing treatment to enhance localized corrosion resistance of pure titanium

Anodic Oxidation Characteristic of Commercial Pure Titanium and Its Corrosion Resistance

The Effect of Potential on Surface Characteristic and Corrosion Resistance of Anodic Oxide Film Formed on Commercial Pure Titanium at the Potentiodynamic-Aging Mode

Corrosion Behavior of TiO2 Film Prepared by Anodic Oxidation Method in Simulated Deep Sea Hydrothermal Region

Corrosion Behavior of Anodic Oxidized TiO 2 Film in Seawater

Corrosion Study of TiO2 Nanotubes Decorated with Ag Silver Nanoparticles Prepared by Photoreduction Process