Morphologies and Magnetic Properties of α-Fe 2 O 3 Nanoparticles with Calcined at Different Temperatures
Xue-Min He,Duan-Qing Chen,Kun-Yu Su,Zhen-Fei Yu,Yi Zhang,Wei Zhong
DOI: https://doi.org/10.1039/d3cp04520j
IF: 3.3
2023-12-21
Physical Chemistry Chemical Physics
Abstract:Different morphologies and sizes of α-Fe 2 O 3 were prepared by the coprecipitation method using polyvinylpyrrolidone as a dispersant. In the preparation process, the homogeneous and dispersed nanoscale FeOOH particles were first obtained by coprecipitation method, and then the FeOOH particles were calcined at high temperature and formed α-Fe 2 O 3 . The growth and aggregation of the α-Fe 2 O 3 particles at different calcination temperatures resulted in α-Fe 2 O 3 powders with diversiform morphology (nanoscale microsphere, pinecone ellipsoidal, polyhedral, and quasi-spherical structure). By analyzing the SEM images, it was inferred that the polyhedral structure of α-Fe 2 O 3 particles was formed by the accumulation and accumulation of rhomboid sheet structures and high temperature growth. In the aspect of magnetic, the samples belong to the canted antiferromagnetic materials, and the morphology, particle size and crystallite size of α-Fe 2 O 3 particles were important factors affecting the coercivity. Among them, when the calcination temperature was increased from 700 °C to 800 °C, the growth rate of particle size was significantly faster than that of grain size, and the coercivity increased substantially from 1411 Oe to 2688 Oe.
chemistry, physical,physics, atomic, molecular & chemical