Microstructural evolution and enhanced magnetic properties of FeCoNiZr x medium entropy alloy films
Zeping Li,Fangfang Wang,Changchun Zhao,Yimin Liao,Ming Gao,Hu Zhang
DOI: https://doi.org/10.1016/j.jallcom.2023.172649
IF: 6.2
2023-11-05
Journal of Alloys and Compounds
Abstract:Medium/High entropy alloys (M/HEAs) based on the FeCoNi system have gained significant attention due to their outstanding magnetic and electrical properties. In this study, the FeCoNiZr x (x = 0, 0.2, 0.4, 0.6, 0.8, 1) MEA films were prepared using the magnetron sputtering method. The effect of Zr on the structure and soft magnetic properties is studied. As the Zr content increases, the films transform from the face-centered cubic (FCC) phase to the amorphous phase. This study shows that FeCoNiZr 0.4 film exhibits excellent combined properties, including a high magnetization saturation (Ms) of 1127.8 emu/cm 3 , a minimum coercivity (Hc) of 0.96 Oe, and a high resistivity of 147 μΩ·cm, which is superior to the Permalloy and soft magnetic materials reported in other articles. Combined structural analyses show that the FeCoNiZr 0.4 film has the finest particle size, amorphous structure, and continuous and uniform magnetic domains, decreasing the pinning effect on magnetic domains. These results enhance the magnetic properties of FeCoNiZr 0.4 film.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering