Enhance the Magnetic Properties of Fe-Si-Al-Cr Flaky Particles by Annealing
L. Deng,Xin Wang,Jiangliang Xie,P. Zhou,N. Zhang
Abstract:Fe-Si-Al-Cr ∞aky particles were used as microwave absorbing material. Iron-Silicon- Aluminum-Chromium ingots with nominal compositions Fe73Si15Al10Cr2 were produced by al- loying the pure elements in an induction melting furnace under argon atmosphere at 0.03MPa, and then the ingots were crushed into irregular shaped particles. As-crushed alloy had been milled by planetary miller for 32h. In order to increase the efiective permeability, the material was annealed under difierent conditions. The morphology of the powders was characterized by scanning electron microscope (SEM). The phases of powders were estimated by X-ray difiract ometer (XRD). The microwave permeability dispersion spectra of annealed powders within a frequency range of 0.5{8GHz was measured. The SEM results showed that particles had been successfully transformed into the ∞aky shape. The average diameter of ∞akes is about 43"m. The average aspect ratio (width/thickness) of ∞akes is about 28. The XRD results showed that the DO3 ordered phase coexisted with fi-Fe(Si,Al,Cr) matrix phase by annealing above 500 - C. When the annealing temperature increased from room temperature to 800 - C, the grain size grown from 10.4nm to its maximum 29.8nm and part of fi-Fe(Si,Al,Cr) matrix phase translated into DO3. The imaginary part of the efiective permeability increased with the annealing temperature, and decreased when the temperature was above 500 - C. The resonance frequency decreased with the annealing temperature, and increased when the temperature was above 400 - C. The efiec- tive permeability of the powders, obtained by 500 - C annealing, had a maximum value of 6.0 at 2.5GHz.
Engineering,Physics,Materials Science