Influence of Fe Content on Lattice, Structural and Magnetic Analyses of BaFe 2+ 2 Fe 3+ 16-x O 27± Hexaferrites Prepared by Facile Ceramic Route Methodology
Jin Tang,Dan Li,Yimin Li,Chen Liu,Jishu Zeng
DOI: https://doi.org/10.1007/s11664-021-09194-y
IF: 2.1
2021-01-01
Journal of Electronic Materials
Abstract:Fe 2 W-type ferrite BaFe 2+ 2 Fe 3+ 16-x O 27± (x =−0.8, −0.4, 0.0, 0.4, 0.8, 1.2) fine powders and magnets were synthesized by a facile ceramic route. The lattice and microstructure of the fine powders were studied by x-ray diffraction (XRD). The results show that a single magnetoplumbite structure is obtained under the condition of Fe change (x =−0.8, −0.4, 0.0, 0.4, 0.8, 1.2). The morphology of the sintered magnet was studied by scanning electron microscopy (SEM). The influence of iron content on the magnetic characteristics of BaFe 2+ 2 Fe 3+ 16-x O 27± was systematically studied by controlling the pre-sintering temperature of 1300°C. The change in the remanence ( B r ) of BaFe 2 2+ Fe 16-x 3+ O 27± magnets with different iron content first increased and then decreased, which confirmed that the change trend of the B r was consistent with the variation in the saturation magnetization ( M s ). Meanwhile, the coercivity ( H cj ) and ( H cb ) of the magnets was consistent with the change characteristics of the coercive force ( H c ) of magnetic powder. At iron change (x) = −0.4, M s , B r , H c , H cj , H cb , and maximum energy product ( (BH) max ) reach maximum.