Abstract:With the rapid development of the petrochemical industry, sulfur-related devices are increasing. In this paper, a fire accident occurred in a petrochemical storage tank of a petrochemical enterprise. Through analysis, we found that the direct cause of the accident was the spontaneous combustion of ferrous sulfide (FeS), which caused the explosion of the oil and gas mixture between the floating disk and the tank top. In addition, we analyzed the corrosion of aluminum floating plates in oil tanks by Scanning Electron Microscope (SEM) and Energy Dispersive Spectrometer (EDS). The analyses showed that although AlMn1 Cu aluminum alloy has high corrosion resistance, the material composition contains impurity elements such as silicon and iron, which weakens the corrosion resistance of aluminum alloy, and the intergranular corrosion and corrosion effects such as pitting corrosion cause cracks to form in the floating disk. The oil and gas that volatilize in the oil tank diffuse through the pores between the floating plate and the top of the tank to form an explosive mixture of oil gas and air. Next, the corrosion products of the manhole cover and the edge of the floating plate were sampled and were analyzed the sulfur and iron contents by elemental analysis. The results showed that the sulfur content in the sample of the manhole of the No. 1 tank was 25.04 wt%, and the sulfur content in the sample at the edge of the floating plate was 7.49 wt%. This was owing to the manhole at the bottom of tank No. 1 is not in contact with air. The edge of the floating plate of tank No. 1 has a low sulfur content due to the long-term contact with air and the burning process during an accident. Using Fault Tree Analysis (FTA), we conclude that the necessary conditions for the accident are appropriate heat storage conditions. The key factors are bad desulfurization effect on the refining process, sulfur in the crude oil, nonresistance of the tank material to corrosion and presence of S2- in the tank. Finally, corresponding countermeasures are proposed.

Cause and measure for equipment corrosion in AS end gas system

Corrosion Types and Measures for Petrochemical Equipment

Cause Analysis and Prevention Measures of Fire and Explosion Caused by Sulfur Corrosion

Corrosion in Atmospheric Distillation Unit Processing Russian Crude Oil and Protection

A New Process of Solveing Corrosion Problem of Refined Liquefied Gas

Investigation into main controlling factors and prediction model of L245NS steel corrosion rate in CO2–O2–SO2–H2S–H2O environment

Corrosion of Sedimentary Liquids on Internal Bottom Plate of Tanks among Coal Liquefaction Process

Analysis of Causes and Protective Measures against Corrosion Perforation in the Shell-Side Outlet Flange of a Sour Water Steam Heater

Synergistic Effect of the Total Acid Number, S, Cl, and H2O on the Corrosion of AISI 1020 in Acidic Environments

Numerical Simulation of Acid Gas Distribution and Corrosion Characteristics in Connecting Pipe of Lean/Rich Amine Heat Exchanger

CORROSION MECHANISM FOR HYDROGENATION SYSTEM EFFLUENT AIR COOLERS

Erosion and intergranular corrosion induced failure of S31254 stainless steel – Case study on Venturi scrubber in a natural gas purification plant

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Corrosion Mechanism of Oil Field Gathering Pipeline Containing Small H2S Impurity

Corrosion Failure Analysis of Stainless Steel Components for Maleic Anhydride Plant

Influence of process conditions on corrosion of equipment in urea plant

Hydrogen Sulfide Corrosion of Metal Equipment in Oil and Gas Field

Corrosion Causes and Corrosion Control Measures for Melamine Quench Tower Lining

Corrosion Evaluation of One Wet Desulfurization Equipment – Flue Gas Desulfurization Unit

A Monitoring Technique for Wet H2S Corrosion in Propane Tank

CORROSION AND PROTECTION OF CONDENSERS IN XUZHOU POWER PLANT