Abstract:In this paper, we report a simple melt impregnation method by using cheap mesophase pitches (MPs) as carbon precursors to prepare ordered mesoporous carbon with ordered graphitized pore walls at low temperature. This facile procedure includes melting MPs at 140 degreesC and impregnation of the melt into hexagonal or bicontinuous cubic mesoporous silica templates. After the removal of silica templates by HF solution, ordered mesoporous carbon materials with replica structures of 2-D hexagonal p6mm or cubic Ia (3) over bard symmetry were derived. The pore walls of the hexagonal mesoporous carbon products are composed of graphitized domains with the (002) crystallographic plane of the graphite perpendicular to the long axis of the carbon nanorods. Theoretical computations show that negatively charged O atoms of Si-OH and Si-O-Si from the surface of mesoporous silica channels can interact with the positive charged H atoms of the MPs, which makes the stacking units incorporate into the pores with the (002) plane vertical to the channels, and finally the oriented periodicity of the graphite domains is formed. N(2) sorption measurements show that the materials possess no micropores. For the bicontinuous cubic mesoporous carbon, HRTEM images show that the material is a true replica framework of la3 ($) over bard symmetry. The graphitized structure of the pore walls seems to have an orientation related to the bicontinuous pore structure, which could not be simply defined based on current TEM results. Graphitized carbon nanofiber bundles with a uniform diameter of about 7 nm were obtained by using Fe(2)O(3) nanoparticle doped mesoporous silica as a template. A spiral graphite structure was observed for the materials. Cyclic voltammetry measurements show low charge/discharge currents for the graphitized materials compared to the amorphous mesoporous carbon, further confirming the anisotropic character of the graphitized mesoporous carbons. The method can be widely applied to the hard-templating synthesis of graphitized carbon nanostructures and other doped carbon nanomaterials.

A Facile Way to Synthesize Ordered Mesoporous Carbon Replicated by Mesoporous Silicas

Facile synthesis of ordered mesoporous carbon with finger citron residue as carbon precursor

Easy synthesis of an ordered mesoporous carbon with a hexagonally packed tubular structure

A simple method to synthesize graphitic mesoporous carbon materials with different structures

Facile Preparation, Structural Control and Spheroidization of Mesoporous Carbons Using Hydrolyzed Water Glass As a Template

Synthesis of Ordered Mesoporous Carbon from Furfuryl Alcohol by Vapor Deposition Polymerization Method

Synthesis of Ordered Mesoporous Carbon from Furfuryl Alcohol as Carbon Source Using Wet Infiltration Method

Synthesis of Carbon Replicas of Sba-1 and Sba-7 Mesoporous Silicas

Electron Microscopy and Nitrogen Adsorption Studies of Film-Type Carbon Replicas with Large Pore Volume Synthesized by Using Colloidal Silica and Sba-15 As Templates

Facile Synthesis of Ordered Mesoporous Carbons with High Thermal Stability by Self-Assembly of Resorcinol-Formaldehyde and Block Copolymers under Highly Acidic Conditions

Synthesis of ordered mesoporous carbon materials using new mesoporous silica as templates

Synthesis of Ordered Three-Dimensional Large-pore Mesoporous Silica and Its Replication to Ordered Nanoporous Carbon

Simplified Novel Synthesis of Ordered Mesoporous Carbon with a Bimodal Pore System

Synthesis of Ordered Mesoporous Carbons Using Resorcinol-Formaldehyde Sol As the Carbon Source and As-synthesized MCM-48 As the Template

An Aqueous Cooperative Assembly Route to Synthesize Ordered Mesoporous Carbons with Controlled Structures and Morphology

A facile aqueous route tosynthesize highly ordered mesoporous carbons with open pore structures

Facile Synthesis of Hierarchically Ordered Porous Carbon Via in Situ Self-Assembly of Colloidal Polymer and Silica Spheres and Its Use As a Catalyst Support

Template Synthesis of Large Pore Ordered Mesoporous Carbon

Synthesis and characterization of mesoporous carbon functionalized with carboxylate groups for a promising adsorbent

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

A Simple Melt Impregnation Method to Synthesize Ordered Mesoporous Carbon and Carbon Nanofiber Bundles with Graphitized Structure from Pitches