Surface segregation and magnetism of an alloy surface: PtNi(0 0 1)
S.Y Choi,Y.S Kwon,S.C Hong,J.I Lee,R.Q Wu
DOI: https://doi.org/10.1016/S0304-8853(00)01104-5
IF: 3.097
2001-01-01
Journal of Magnetism and Magnetic Materials
Abstract:In this work we studied the atomic segregation and magnetization of the PtNi(0 0 1) surface, using the full-potential linearized augmented plane wave (FLAPW) method with GGA. Results of total energies for different film thicknesses (1, 3, 5, and 7-layers) and surface compositions (with 100%, 50% and 0% of Pt concentration) indicate that the Pt-100% terminated surface is the most stable configuration for PtNi(0 0 1), a result which is consistent with the experimental data. The calculated magnetic moments of surface (with Pt atoms) and subsurface (with Ni atoms) layers are 0.41 and 0.85 μ B , respectively. The d-band hybridization between Ni and Pt atoms was found to play an important role in determining the magnetism. Keywords Band calculation Magnetic moments—calculated Surface Alloys Surface magnetism has attracted extensive experimental and theoretical studies due to its applicability to magnetic information storage media and devices. As known, magnetism at a surface differs significantly from that in the bulk, due to the effects of surface states and band narrowing. Although Ni is a typical ferromagnetic element and Pt has sizable magnetization in various environments [1,2] , the ordered equiatomic PtNi alloy is found to be nonmagnetic both experimentally [3] and theoretically through rough tight-binding calculations [4] . For the atomically disordered alloy, the magnetization depends sensitively on the Ni concentration. The critical composition of Ni to induce the onset of ferromagnetism is about 40% [3] . Hence, we can expect that the surface of the ordered equiatomic PtNi alloy is ferromagnetic while its bulk form is close to being magnetic. Furthermore, PtNi alloy has been known to show an interesting surface segregation phenomenon: with Pt enrichment on the (1 1 1) and (0 0 1) surfaces and Ni enrichment on the (1 1 0) surface [5,6] . In this study, we investigated the atomic segregation and magnetism at the PtNi(0 0 1) surface, by carrying out first principles calculations with the full-potential linearized augmented plane wave (FLAPW) method [7] . The systems were simulated by slabs with varying thicknesses (1, 3, 5, and 7-layers) and surface compositions (Pt-100%, 50%, and 0%). The ordered bulk PtNi has a L1 0 tetragonal structure with a c / a ratio of 0.939 at low temperature while a geometric cubic structure ( c / a =1) is adopted at high temperature. Here we chose the cubic lattice with a=3.747 Å [8] for computational convenience and also to minimize the effects of lattice distortion due to the surface segregation 1 1 In the L1 0 tetragonal structure the 2D lattice of the Pt-50% surface is different from that of the Pt-100% or 0% surface. The difference may introduce an error in the direct comparison among the total energies . No relaxation and reconstruction at the surface were assumed. Six special k -points within the irreducible Brillouin zone (BZ) and about 680 variational basis functions were used. The Kohn–Sham equations with GGA [9] were solved self-consistently employing the FLAPW method [7] . The core electrons were treated fully relativistically, whereas the valence electrons treated semi-relativistically. Self-consistency was assumed when the rms differences between the input and output spin and charge densities were less than 2×10 −5 electrons/(a.u.) 3 The surface energy, Δ E surface , can be obtained by calculating total energies of two slabs with different numbers as, (1) E bulk ≈ [E(7L)−E(5L)] 2 , (2) Δ E surface = [E(7L)−7×E bulk ] 2 . where E (5 L ) and E (7 L ) are the total energies of the slabs with 5- and 7-layers, respectively. For the Pt-50% surface which has the same composition over all layers, the surface energy obtained through Eqs. (1) and (2) is 1.23 eV. For the Pt-100% and Ni-100% surfaces with the oscillatory composition profiles, however, the surface energy cannot be calculated directly from Eq. (2) because the portion of Pt in E bulk cannot be separated from that of Ni. Nevertheless, the average of surface energies of Pt-100% and Ni-100% can be calculated from the total energies of the 7-layers as (3) Δ E surface = [E 100% Ni (7L)+E 100% Pt (7L)−14×E bulk ] 4 . This average surface energy is 1.15 eV , 0.08 eV lower than that of Pt-50%. It suggests that either Pt-100% or Ni-100% surface is energetically more stable compared to the 50–50% surface. To find out which surface (Pt-100% or Ni-100%) is the most stable configuration, we calculated the adsorption energy, E ad (defined as E ad = E adsorbed − E substrate − E adlayer ), of a Pt monolayer on the Ni-100% surface and vice versa. The calculated values of E ad are −3.73 and −3.16 eV for Pt/Ni-100% surface and Ni/Pt-100% surface, respectively. Since the two adsorption systems have the same interfacial condition, the difference in E ad (−0.57 eV) should come from the difference between their surface energies. Combining with the results of the average surface energy (1.15 eV), the surface energies of Pt-100% and Ni-100% surfaces can be deduced to be 0.87 and 1.44 eV, respectively. This result indicates that the Pt-100% surface is the most favorable configuration for PtNi(0 0 1), a result which is consistent with experimental observation. In Table 1 , the calculated magnetic moments and total energy differences between the FM and PM states of 7-layer films are listed for different configurations. The magnetic moments of Ni(S) at the Ni-100% and Pt-50% surfaces are 0.77 and 0.81 μ B . They are enhanced by 10% and 16% compared to that of the clean Ni(0 0 1) [10] , respectively. For the Pt-100% and Pt-50% surfaces, Pt(S) have sizable magnetic moments of 0.41 and 0.35 μ B , respectively. It is noticeable that the subsurface Ni atom in the Pt-100% surface has the largest magnetic moment (0.85 μ B ), which is enhanced by 50% from that of bulk Ni (0.58 μ B ). It suggests the importance of change in band hybridization on the Ni and Pt magnetization. In conclusion, we investigated the surface segregation and magnetization of PtNi(0 0 1), using the FLAPW method based on the GGA. Total energy calculations for films with different thicknesses and chemical compositions indicate that the Pt-100% surface is the energetically most stable case. This is consistent with the experimental observation of the Pt-enrichment at the PtNi(0 0 1) surface. The strong hybridization between Ni- and Pt-d bands enhances the magnetic moments of both Ni and Pt atoms. The subsurface Ni atom in the Pt-100% terminated PtNi(0 0 1) surface has a magnetic moment of 0.85 μ B , about 50% larger compared to that of the bulk Ni 0.58 μ B ). This work was supported by ASSRC at Yonsei University and eSSC at POSTECH. References [1] S.C. Hong, W.D. Kim, J.S. Kim, unpublished. [2] R. Wu C. Li A.J. Freeman J. Magn. Magn. Mater. 99 1991 71 [3] C.E. Dahmani Phys. Rev. Lett. 55 1985 1208 [4] Y. Ohta M. Miyauchi M. Shimizu J. Phys.: Condens. Matter 1 1989 2637 [5] Jikeun Seo W.K. Han J. Korean. Phys. Soc. 28 1995 S600 [6] D. Dufayard R. Baudoing Y. Gauthier Surf. Sci. 233 1990 223 [7] M. Weinert E. Wimmer A.J. Freeman Phys. Rev. B 26 1982 4571 [8] W.B. Pearson, A Handbook of Lattice Spacing and Structure of Metals and Alloys, Pergamon Press, London, 1967. [9] J.P. Perdew K. Burke M. Ernzerhof Phys. Rev. Lett. 77 1996 3865 [10] E. Wimmer A.J. Freeman H. Krakauer Phys. Rev. B 30 1984 3113