Abstract:The accepted mechanism of alginate gelation at ambient temperature is by formation of egg-box junctions between pairs of polyguluronate chain sequences and an included array of site-bound calcium ions. We now present evidence (circular dichroism and low-amplitude mechanical spectroscopy data) of similar regular interactions at high temperatures where all the active ingredients (alginate, salt and sequestrant) are hydrated in a hot medium. During controlled cooling, a second transition is obtained at low temperatures, which may be attributed to the lateral interaction of dimeric chains and thus the development of an extended, three-dimensional network. A subsequent temperature increase melts the second wave of structure formation, thus producing substantial thermal hysteresis, but preserves the ‘weak gel’ properties of the alginate-calcium reaction observed at elevated temperatures. At levels of salt higher than 40% calcium conversion aggregation can occur even at 90°C, leading to precipitation rather than a homogenous network. Prolonged refrigeration (72 h at 4–5°C) sustains a gradual molecular rearrangement to a self-supporting (visual evidence), firmer (frequency sweeps) network. Surprisingly, the strongest high guluronate alginate is not only more elastic than its low molecular weight counterpart (strain sweeps in dynamic oscillation) but it also exhibits higher yield strain on compression testing than the high molecular weight, high mannuronate sample. The distinct differences in the long-range properties of high guluronate and high mannuronate alginate samples with comparable molecular weights might serve as a guide for the development of reformed products with the desired characteristics.

Study on the Preparation of Medical Alginate Calcium Fiber

Fabrication and Characterization of Absorbent and Antibacterial Alginate Fibers Loaded with Sulfanilamide

Preparation, Structure and Properties of High Strength Alginate Fiber

Mechanical properties of calcium alginate fibers produced with a microfluidic device

Preparation and Properties of Nano-Silica/Calcium Alginate Blend Fibers

Characterization and Functional Assessment of Alginate Fibers Prepared by Metal-Calcium Ion Complex Coagulation Bath.

Preparation and Characterization of Composite Hydrogel Beads Containing Sericin and Sodium Alginate

Study on the preparation and performance of calcium alginate/gelatin composite membranes

Fabrication and Characterization of Alginate Fibers by Wet-Spinning

In Situ Modification of Alginate Fibers by Nano-montmorillonite for Enhancing the Mechanical Properties

Preparation and Properties of Alginate Salt Fibers: an Inherent Flame-Retardant, Biodegradable Fiber

Preparation of Hollow Calcium Alginate Microfiber Composited with Silicon Dioxide

Effects of Molecular Weight and Guluronic Acid/Mannuronic Acid Ratio on the Rheological Behavior and Stabilizing Property of Sodium Alginate

Structural and textural properties of calcium induced, hot-made alginate gels

Physico-chemical properties and rheology of alginate gel beads formed with various divalent cations

Impact of cotton fiber percentage and length on mechanical behavior of cotton/alginate composite hydrogel fiber

Fabrication, Property and Application of Calcium Alginate Fiber: A Review

Influence of Alginate Properties and Calcium Chloride Concentration on Alginate Bead Reticulation and Size: A Phenomenological Approach

Cellulose Nanofibrils/Alginates Double-Network Composites: Effects of Interfibrillar Interaction and G/M Ratio of Alginates on Mechanical Performance

The conversion of calcium alginate fibers into alginic acid fibers and sodium alginate fibers

Effect of SiO2, PVA and glycerol concentrations on chemical and mechanical properties of alginate-based films