Abstract:C/C materials represent as materials with specific performance, therefore they are applied in various industries. It is essential to figure out the paths to predict, to provide and to enhance their properties to obtain high performance products. It is well known that strong matrix/reinforcer adhesion provides better strength utilization and therefore better properties for the majority of composite materials of all types (Heim in Compos Part B Eng 54:365–370, 2013), (Hancock and Cuthbertson in J Mater Sci 5:762–768, 1970), (Yang et al. in Polymers 13:2764, 2021). However some researchers note that strong adhesion in the materials that are exposed to high temperatures leads to cracking and significant properties degradation (Vignoles et al. in The Control of interphases in carbon and ceramic matrix composites, Wiley, Hoboken, 2012), (Zhang et al. in Compos Struct 340, 2024). In this work, the effect of the pyrocarbon layer applied on the surface of carbon fibers used for reinforcement of formaldehyde novolac resin based carbon/carbon (C/C) material prepregs was investigated. For the first time we used this effect to prove that lower matrix/reinforcer adhesion in C/C materials prepregs leads to better material behavior during pyrolysis, which results in higher mechanical properties of the pyrolised samples in comparison with the samples demonstrating stronger matrix/reinforcer adhesion. The prepregs were thermally treated at various temperatures, the physical and mechanical performance evolution of the prepregs at different carbonization stages were analyzed. Comparative study of the features of the prepregs with pyrocarbon coated and uncoated carbon fiber as a reinforcement were carried out. The damping effect of the pyrocarbon on the fiber surface were advertised, allowing to mitigate the carbonization-caused effects. The prepregs reinforced with pyrocarbon-modified carbon fibers demonstrated lower cracking performance and higher mechanical performance comparing with the uncoated fiber reinforced prepregs.

Deposition mechanism and microstructure of pyrocarbon prepared by chemical vapor infiltration with kerosene as precursor

Kinetics of thermal gradient chemical vapor infiltration of large-size carbon/carbon composites with vaporized kerosene

Preparation of C/C Composites by Thermal Gradient Chemical Vapor Infiltration with Vaporized Kerosene As a Precursor

Microstructure and Electrical Resistivity of Carbon/carbon Composites Prepared by Thermal Gradient Chemical Vapor Infiltration

Micro- and nano-structural investigations of C/C composites

Deposition Kinetics and Mechanism of Pyrocarbon for Electromagnetic-Coupling Chemical Vapor Infiltration Process

Correlation of the permeability and porosity development of carbon/carbon composites during pyrolysis

Novel Carbon Felt Composites with Pyrocarbon Deposited on Carbon Fiber: Hierarchical Microstructure for Improved Phenol-Adsorption

Molecular Insights into the Initial Formation of Pyrolytic Carbon Upon Carbon Fiber Surface

Modeling of Carbon Deposition from Propane in Chemical Vapor Infiltration

Chemical Supercritical Fluid Infiltration of Pyrocarbon with Thermal Gradients: Deposition Kinetics and Multiphysics Modeling

Research on Temperature Field of Kerosene when Preparing Carbon/Carbon Composites by Chemical Liquid Deposition

Rapid Chemical Vapor Infiltration of C/C Composites

Numerical Study of Fluid Flows and Heat Transfer of Aviation Kerosene with Consideration of Fuel Pyrolysis and Surface Coking at Supercritical Pressures

Improvement of Chemical Liquid Vaporized Infiltration Process for Fast Densification of Carbon/Carbon Composites

Comprehensive study of thermal degradation behavior of carbon fiber flexible sucker rods: Product characteristics, kinetics and thermodynamics

Study on the Formation and Dissipation Mechanism of Gas Phase Products During Rapid Pyrolysis of Superfine Pulverized Coal in Entrained Flow Reactor

Reinforcement of C/C materials prepregs with pyrocarbon coated carbon fiber as the way to improve the prepregs properties after pyrolysis

Improvement of Film Boiling Chemical Vapor Infiltration Process for Fabrication of Large Size C/C Composite

Microstructure of the pyrocarbon in aligned carbon nanotube/carbon composites

The effect of carbon nanotubes on the microstructure and morphology of pyrolytic carbon matrices of C–C composites obtained by CVI