Abstract:To evaluate the residual service performance of corroded high-tensile steel wires, a batch of in situ wires that had served for 13 years in the hangers of an arch bridge was investigated. Four types of corroded wires were derived from the in situ wires by placing them in the indoor environment for 1.5 years (Type A) or treating them in an alternate dry-wet environment for 0.25-1.5 years (Types B, C, and D). The mechanical properties of the corroded wires were investigated with tensile and fatigue tests, and the fracture characteristics were observed. Fatigue tests on Type A wires with different stress ranges were conducted, and the stress intensity factor range Delta K-p at the bottom of crack-initiation pits was analyzed. According to the S-N curve for Type A wires, the crack-propagation characteristics of steel wires were investigated. The linear elastic fracture mechanics (LEFM) approach was used to predict the residual life of corroded wires in two systems of arch bridges. The tests show that the ultimate strain of corroded wires decreased with an increase in degree of corrosion. The fatigue properties of wires were found to degrade significantly at the early corrosion stage, and the degradation rate slowed down with further development of corrosion. The correlation between the fatigue life and the stress intensity factor range DKp at the bottom of corrosion pits shows that larger pitting size tended to have shorter life under the same stress range, and fatigue cracks were difficult to initiate at the corrosion pits below the fatigue threshold. The crack-growth parameters of the Paris law identified from the S-N curve of Type A wires were m = 2.87, C = 8 x 10(-12) under the stress ratio R = 0.5. The residual life predicted by LEFM shows that in a dry environment, corroded wires with an initial pitting depth of 0.6 mm can serve for more than 30 years in arch-beam combination-system bridges, whereas they can only serve for 5 years in floating-system arch bridges.

Anti-corrosion Performance of Galvanized Steel Framing in Residential Environments in North America

Experimental Study and Residual Performance Evaluation of Corroded High-Tensile Steel Wires

The Evolution of the Corrosion Mechanism of Structural Steel Exposed to the Urban Industrial Atmosphere for Seven Years

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Study on the durability of light-weight steel structures with gabled frame in coastal areas

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Corrosion Resistance of Zinc and Zinc-Aluminum-Magnesium Coatings in Atmosphere on the Territory of Russia

THE STATE OF THE ART OF CONCRETE STRUCTURE DURABILITY MONITORING AND RESTORATION

Steel Bridge-Coating Systems and Their Environmental Impacts: Current Practices and Future Trends

Research on Rust Removal and Rust Prevention Method of Super-High-Rise Steel Structure

Continuous Galvanized Reinforcing Steel in Concrete Structures

Electrochemical Characterization of Steel Bridge Welds under Simulated Durability Test

Architecture of medium- and multistoried residential buildings with steel framework

A Research on Steel Residential Building Comprehensive Evaluation Based on Layer Analysis and Value Engineering Method:Taking Second Periods of Hangzhou Taihe Garden as an Example

Design of Light-Weight Steel Residential and Its Economic Analysis

RESEARCH ON THE ENERGY-SAVING DESIGN SCHEMES OF LIGHT GAUGE STEEL-FRAMED COMPOSITE WALLS OF RESIDENTIAL CONSTRUCTION

A Method for Predicting the Corrosion Behavior of Structural Steel under Atmosphere

Anti-Corrosion Reinforcements Using Coating Technologies—A Review

Corrosion Resistance of High Performance Weathering Steel for Bridge Building Applications

Study on Corrosion Resistance of Low-Temperature Sintered Chemically Reactive Enamel Coated Rebars

The assessment of structural behaviours of steel framing system – affordable house system design