Abstract:Resistive, magnetoresistive and magnetic properties of four kinds of pressed CrO2 powders, synthesized by hydrothermal method of chromic anhydride have been investigated. The particles in powders constituted of rounded particles (diameter 120 nm) or needle-shaped crystals with an average diameter of 22.9 nm and average length of 302 nm. All of the particles had a surface dielectric shell of varying thickness and different types (such as oxyhydroxide -CrOOH or chromium oxide Cr2O3). For all the samples at low temperatures we found non-metallic temperature dependence of resistivity and giant negative magnetoresistance (MR). The maximum value of MR at low temperatures (T \approx 5 K) is \approx 37% in relatively small fields (0.5 T). At higher temperatures there was a rapid decrease of MR (up to \approx 1% / T at T \approx 200 K). The main objective of this work was studying the influence of properties and thickness of the intergranular dielectric layers, as well as CrO2 particle shape, on the magnitude of the tunneling resistance and MR of the pressed powder. The new results obtained in this study include: (1) detection at low temperatures in powders with needle-like particles a new type of MR hysteresis, and nonmonotonic MR behaviour with increasing magnetic field (absolute value of the MR at first grows rather rapidly with the field, and then begins diminishing markedly, forming a maximum), and (2) detection of non-monotonic temperature dependence, where - a field in which the resistance in a magnetic field has a maximum, as well as finding discrepancies in values of and coercivity fields, (3) detection of the anisotropy of MR, depending on the relative orientation of the transport current and the magnetic field, (4) a new method of synthesis, to regulate the thickness of dielectric coating.

Shape-controlled synthesis of high-purity CrO2 under HTHP

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Shape-Controlled Synthesis of Mnwo4 Nanocrystals by A Surfactant-Free Hydrothermal Method

Preparation of One-Dimensional Diluted Magnetic Semiconducting Cr0.046zn0.954o and Properties Tuning with H-2 Atmospheric Annealing

Synthesis of Single-Crystal Perovskite PbCrO3through a New Reaction Route at High Pressure

Enhanced Formation of Α-Al2o3 at Low Temperature on Cr/Al Coating by Controlling Oxygen Partial Pressure

Controllable Synthesis of TiO 2 Single Crystals with Tunable Shapes Using Ammonium-Exchanged Titanate Nanowires as Precursors

Shape-controlled synthesis of PbCrO 4 micro/nanostructures and their luminescent properties

Preparation and Magnetic Properties of Submicron CrO2 Thin Film on Poly-Crystal TiO2 Film

A Method Probing High-Temperature Oxidation Behavior of Crystalline Materials

Resistive and magnetoresistive properties of CrO2 pressed powders with different types of inter-granular dielectric layers

Structure and magnetic properties of Cr-doped ZnO nanoparticles prepared under high magnetic field

Transport and magnetotransport properties of cold-pressed CrO2 powder

In-situ Observation of Single-Phase Compositionally-Complex Oxide Formation During High-Pressure and High-Temperature Synthesis

In Situ Phase Transition Study of Nano- and Coarse-Grained Tio(2) under High Pressure/Temperature Conditions

Morphology-Controlled Synthesis of Co3o4 by One Step Template-Free Hydrothermal Method

etic and electronic properties of CrO 2 at multimegabar pressures

Shape-Controlled Synthesis of Single-Crystalline Cdco3 and Corresponding Porous Cdo Nanostructures

Hydrothermal synthesis and characterization of (Zr1−xSnx)TiO4 (x = 0.05–0.20) powders

The pyrochlore Ho2Ti2O7: Synthesis, crystal growth and stoichiometry