Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Fabrication of Oriented TiO2-Based Nanotube Array Thin Films

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Structure-tunable Synthesis and Structural Stabilities of the Multilayered Titanate Nanotube Thin Films Grown on Titanium Metal Surface

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Facile Fabrication, Characterization, and Enhanced Photoelectrocatalytic Degradation Performance of Highly Oriented Tio2 Nanotube Arrays

Low-Temperature Synthesis of High-Ordered Anatase Tio2 Nanotube Array Films Coated with Exposed {001} Nanofacets

A facile solution route to deposit TiO2 nanowire arrays on arbitrary substrates.

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

Fabrication of multi-sectional TiO 2 nanotube arrays by anodization

Fabrication of Titanium Oxide Nanotube Arrays by Anodic Oxidation

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

In-situ template synthesis of TiO2 nanotube array films

In-situ template synthesis of TiO2 nanotube array films on Al substrates

Oriented Array of TiO2 Nanorods

Aligned metal oxide nanotube arrays: key-aspects of anodic TiO2 nanotube formation and properties

Titanium oxide nanotube arrays prepared by anodic oxidation

Fabrication of Highly-Oriented TiO2 Nanotube Arrays and Its Application in Dye-Sensitized Solar Cells

Fabrication and Photo-Electrocatalytic Properties of Highly Oriented Titania Nanotube Arrays with {1 0 1} Crystal Face

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.