Abstract:Objective:To investigate the effect of a porous calcium phosphate/bone matrix gelatin (BMG) composite cement (hereinafter referred to as the "porous composite cement") for repairing lumbar vertebral bone defect in a rabbit model. Methods:BMG was extracted from adult New Zealand rabbits according to the Urist's method. Poly (lactic-co-glycolic) acid (PLGA) microsphere was prepared by W/O/W double emulsion method. The porous composite cement was developed by using calcium phosphate cement (CPC) composited with BMG and PLGA microsphere. The physicochemical characterizations of the porous composite cement were assessed by anti-washout property, porosity, and biomechanical experiment, also compared with the CPC. Thirty 2-month-old New Zealand rabbits were used to construct vertebral bone defect at L 3 in size of 4 mm×3 mm×3 mm. Then, the bone defect was repaired with porous composite cement (experimental group, n=15) or CPC (control group, n=15). At 4, 8, and 12 weeks after implantation, each bone specimen was assessed by X-ray films for bone fusion, micro-CT for bone mineral density (BMD), bone volume fraction (BVF), trabecular thickness (Tb. Th.), trabecular number (Tb.N.), and trabecular spacing (Tb. Sp.), and histological section with toluidine blue staining for new-born bone formation. Results:The study demonstrated well anti-washout property in 2 groups. The porous composite cement has 55.06%±1.18% of porosity and (51.63±6.73) MPa of compressive strength. The CPC has 49.38%±1.75% of porosity and (63.34±3.27) MPa of compressive strength. There were significant differences in porosity and compressive strength between different cements ( t=4.254, P=0.006; t=2.476, P=0.034). X-ray films revealed that the zone between the cement and host bone gradually blurred with the time extending. At 12 weeks after implantation, the zone was disappeared in the experimental group, but clear in the control group. There were significant differences in BMD, BVF, Tb. Th., Tb. N., and Tb. Sp. between 2 groups at each time point ( P<0.05). Histological observation revealed that there was new-born bone in the cement with the time extending in 2 groups. Among them, bony connection was observed between the new-born bone and the host in the experimental group, which was prior to the control group. Conclusion:The porous composite cement has dual bioactivity of osteoinductivity and osteoconductivity, which are effective to promote bone defect healing and reconstruction.

In Vivo Evaluation of Injectable Calcium Sulfate Bone Cement in the Defect of Ovariectomized Rat

Experimental study on implantation of injectable calcium sulphate to repair trabeculae of proximal femur of osteoporotic rats

Augmentation of Screw Fixation with Injectable Calcium Sulfate Bone Cement in Ovariectomized Rats.

Enhanced bone formation by strontium modified calcium sulfate hemihydrate in ovariectomized rat critical-size calvarial defects.

Effects of simvastatin loaded calcium sulfate on tibial bone defect healing in ovariectomized rats

Biomechanical Evaluation of Repairation of Cancellous Bone Defect with Calcium Sulphate

Bone Density of Rabbit Femoral Cancellous Bone Defect after Calcium Sulphate Implantation

In vivo assessment of bone repair by an injectable nanocomposite scaffold for local co-delivery of autologous platelet-rich plasma and calcitonin in a rat model

Experimental Study of in vivo Degradation, Absorption and Osteogenesis of Injected Absorbable Polyamine Acid/Calcium Sulfate Composites

Calcium sulfate bone cement with or without injectable polyamino acid for goat vertebral defects:a comparative experiment

Effects of strontium-modified calcium phosphate cement combined with bone morphogenetic protein-2 on osteoporotic bone defects healing in rats

Observation on the Role of Osteoporotic Vertebra Augmented with Calcium Sulfate Cement in Vivo

Bone Augmentation in an Osteoporosis Rat Model Via a Single Local Injection of Simvastatin

Repairing mechanism of mechanical microdamage in the cortical bone of rats

Effect of osteoporosis induced by ovariectomy on vertebral bone defect/fracture in rat

In vivo degradation,absorption and osteogenesis of injectable and absorbable polyamine acid/calcium sulfate composites

Study on the clinical effect of calcium sulfate on the repair of bone defect

Experiment of Porous Calcium Phosphate/bone Matrix Gelatin Composite Cement for Repairing Lumbar Vertebral Bone Defect in Rabbit

The Ability of Biodegradable Thermosensitive Hydrogel Composite Calcium-Silicon-Based Bioactive Bone Cement in Promoting Osteogenesis and Repairing Rabbit Distal Femoral Defects

Chemical Stability-Sensitive Osteoconductive Performance Of Octacalcium Phosphate Bone Substitute In An Ovariectomized Rat Tibia Defect

Histology study of calcium phosphate cement in repairing goat experimental lateral tibial plateau compression fracture