Abstract:The rapid, microwave-assisted aerobic synthesis of silver nanowires based on the polyol method is described. Benchtop dissolution of NaCl and AgNO3 (ratio 1:6 to 1:3) in ethylene glycol and subsequent heating using microwave irradiation (300 W) in the presence of polyvinylpyrrolidone generates Ag nanowires in similar to 80% yield in 3.5 min. Upon purification, microscopy (TEM, SEM) and powder X-ray diffraction reveal a uniform set of crystalline Ag nanowires with dimensions of 45 nm x 4-12 mu m. Wire formation is highly dependent upon the microwave heating power, time, and NaCl:AgNO3 ratio because of the rapid heating process and the presence of O-2 as an etching coreagent. Extended microwave heating causes the wires to fuse if in proximity or degrade to shorter wires presumably via the etching reaction. In the absence of O-2/Cl-, the wires melt upon extended microwave heating (> 4 min), suggesting that nanowire melting may contribute to the observed morphology under etching conditions. Compared to existing wet-chemical methods using traditional heating techniques, microwave irradiation not only rapidly heats, but dielectric heating of the growing wires also occurs, resulting in accelerated deposition of Ag-0 at the wire ends. Furthermore, this high yielding preparation does not require any external seed crystals, precursors, or mechanical stirring and is conducted under ambient O-2 conditions, leading to significant potential for the large-scale fabrication of Ag nanowires using this simple approach.

Synthesis and Characterization of Nanowires of Linearly Stacked Silver Particles

Silver Nanowires Eelectrodeposited from Reverse Hexagonal Liquid Crystals

Synthesis, characterization and self-assembly of silver nanowires

Synthesis of single-crystalline silver sulfide nanowires by diffusion in porous anodic aluminium oxide template

Template preparation of high-density, and large-area Ag nanowire array by acetaldehyde reduction

Sonochemical Synthesis of Amorphous Long Silver Sulfide Nanowires

Convenient, Rapid Synthesis of Ag Nanowires

Growth of Silver Nanowires from Solutions: a Cyclic Penta-Twinned-crystal Growth Mechanism.

Single-crystal silver nanowires: Preparation and Surface-enhanced Raman Scattering (SERS) property

Silver nanowires with five-fold symmetric cross-section

Controlled Growth And Phase Transition Of Silver Nanowires With Dense Lengthwise Twins And Stacking Faults

Low-Temperature Synthesis of Single Crystalline Ag2S Nanowires on Silver Substrates

Single-crystalline Silver Nanowire Arrays Directly Synthesized Onto Substrates by Template-Assisted Chemical Wetting

A template-free oxide reduction route to silver nanowires

Composition-Dependent Formation of Platinum Silver Nanowires

Synthesis of ultra-long silver nanowires and the joining of silver networks

Conditions for Synthesis of Uniform Ag Nanowires via Chemical Reduction Process

Synthesis and Characterizing of High Aspect Ratio Silver Nanowires by Polyol Process

Synthesis and process condition of high aspect ratio silver nanowires

Synthesis of Silver Sulfide Nanowires: Variation of the Morphology and Structure

The Preparation of Anodic Aluminum Oxide Ceramic Template and the Fabrication of Silver Nanowires