Abstract:Template-assisted synthesis is a facile way of growing various one-dimensional nanostructures. Among various nanoporous templates, anodic aluminium oxide (AAO) is most commonly used. In this work, the kinetics of silver nanowire growth by electrodeposition in AAO templates was investigated. The AAO templates were fabricated using the standard two-step anodisation process. The geometrical features of the fabricated templates, such as pore diameter (55 nm), interpore distance (115 nm), wall thickness (27 nm), porosity (19.87 %), and pore density were obtained using scanning electron microscopy. The oxide layer at the bottom of the pores was modified by the barrier layer thinning process and chemical etching in order to facilitate uniform metal deposition. This was followed by pore widening to increase the diameter of the pores to 65 nm to enhance deposition. Interpore distance increased to 119.8 nm and wall thickness remained almost constant at 27.7 nm. Silver was deposited using conventional electrodeposition in constant current mode. Deposition parameters such as time, current, solution concentration, and temperature were systematically investigated. For each deposition, the efficiency of the process was calculated by considering the filling fraction of the pores and the average length of the wires, all of which were measured from the SEM images. A linear growth versus time was observed within the parameter range. From the experiments, it was observed that decreasing the current, increasing the deposition temperature, and depositing for longer duration increased the average length of the nanowires. The use of electrodeposition to grow metallic nanowires can be extended to other pure metal and alloy systems.

Synthesis of single-crystalline silver sulfide nanowires by diffusion in porous anodic aluminium oxide template

Electrochemical synthesis of silver oxide nanowires, microplatelets and application as SERS substrate precursors

Sonochemical Synthesis of Amorphous Long Silver Sulfide Nanowires

Template preparation of high-density, and large-area Ag nanowire array by acetaldehyde reduction

Single-crystal silver nanowires: Preparation and Surface-enhanced Raman Scattering (SERS) property

Single-crystalline Silver Nanowire Arrays Directly Synthesized Onto Substrates by Template-Assisted Chemical Wetting

Synthesis of silver sulfide nanowires in ethylene glycol through a sacrificial templating route

Silver Nanowires Eelectrodeposited from Reverse Hexagonal Liquid Crystals

Low-Temperature Synthesis of Single Crystalline Ag2S Nanowires on Silver Substrates

The Preparation of Anodic Aluminum Oxide Ceramic Template and the Fabrication of Silver Nanowires

Synthesis of Silver Sulfide Nanowires: Variation of the Morphology and Structure

Convenient, Rapid Synthesis of Ag Nanowires

Template-assisted growth of silver nanowires by electrodeposition

Synthesis of Single Crystal Metal Sulfide Nanowires and Nanowire Arrays by Chemical Precipitation in Templates

Electrochemical Fabrication of Ordered Ag2S Nanowire Arrays

Photochemical Synthesis of Au and Ag Nanowires on a Porous Aluminum Oxide Template

Synthesis and Characterization of High Density and High Aspect Ratio Ag2S Nanoparticle Nanowires from a Paired Cell Method

A Simple and Effective Route for the Synthesis of Crystalline Silver Nanorods and Nanowires

A Simple Route to Large-Scale Synthesis of Silver Sulfide Nanowires

Synthesis of Silver Dendritic Hierarchical Structures and Transformation into Silver Nanobelts Through an Ultrasonic Process

Highly Ordered ZnS Nanowire Arrays Embedded in Anodic Alumina Membrane by a Hydrothermal Method with Double Diffusion