Preparation and crystallization behaviour of PP/PP-g-MAH/Org-MMT nanocomposite

Weibing Xu,Guodong Liang,Hongbo Zhai,Shupei Tang,Guopei Hang,Wei-Ping Pan

DOI: https://doi.org/10.1016/S0014-3057(03)00015-6

IF: 6

2003-01-01

European Polymer Journal

Abstract:The melt-direct intercalation method was employed to prepare polypropylene (PP)/maleic anhydride grafted polypropylene (PP-g-MAH)/organic-montmorillonite (Org-MMT), X-ray diffractometer was used to investigate the intercalation effect and crystallite size in composites and TEM micrograph to observe the dispersion of Org-MMT interlayers in polypropylene. The results showed that by introducing maleated polypropylene in PP/Org-MMT composite, macromolecule segments had intercalated into interlayer space of Org-MMT. As a result, Org-MMT interlayers were dispersed evenly in polypropylene and PP/PP-g-MAH/Org-MMT nanocomposite was synthesized. The crystallite size of nanocomposite perpendicular to the crystalline plane such as (040), (130), (111), (041) is smaller than that of pristine PP, which indicated that the crystallite size of PP in nanocomposite can be diminished by adding PP-g-MAH and Org-MMT in PP. Moreover, the nonisothermal crystallization kinetics of PP and PP/PP-g-MAH/Org-MMT nanocomposite was investigated by differential scanning calorimetry (DSC) with various cooling rates. The Avrami analysis modified by Jeziorny, Ozawa method and a method developed by Liu were employed to describe the nonisothermal crystallization process of these samples. The difference in the exponent n between PP and nanocomposite, indicated that nonisothermal kinetic crystallization corresponded to tridimensional growth with heterogeneous nucleation. The values of half-time, Zc, F(T) and K(T) showed that the crystallization rate of composites was faster than that of PP at a given cooling rate.