Abstract:In this article, we present a study of a new glass system: lead–germanium–tellurite glasses in the form of 0.05K2O–0.1ZnO–0.1BaO–0.2PbO–xGeO2–(0.55 -x)TeO2 with x = 0.1, 0.2, 0.3, 0.4, 0.5, and 0.55. Differential temperature analysis of this glass system shows that increasing GeO2 content raises the glass transition temperature (Tg) and suppresses the crystallization tendency in a large temperature range from Tg to the glass melting temperature. The maximum vibrational frequency is intermediate between germanate and fluoride glasses, in the range of 750 cm−1 to 820 cm−1. Subsequently, Optical absorption, photoluminescence, and upconversion fluorescence were measured for Yb3+, Er3+ co-doped lead–tellurium–germanate glasses. It was found that the full width at half-maximum of the fluorescence spectrum at 1534 nm decreases and the measured radiative lifetime increases with the replacement of TeO2 by GeO2. Excitation at 976 nm into the glass system leads to an intense green emission and a relatively weak red emission. With the addition of GeO2, the increase of red fluorescence and the decrease of green emission in intensity are due to the increase of nonradiative transition rates between the4S3/2 and4F9/2 states of Er3+ ions. The quadratic dependence of the green and red emissions on excitation power indicates that two-photon absorption process occurs in this glass system excited at 976 nm.

Spectroscopic Properties of Er3+/Yb3+ Co-Doped Germanium Tellurite Bismuthate Potassium Glass

Upconversion Luminescence Property of Er3+ and Yb3+ Co-doped Germanium Silicate Glass

Thermal Analysis and Optical Transition of Yb3+, Er3+ Co-Doped Lead–germanium–tellurite Glasses

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Spectroscopic Properties of Er3+ and Yb3+ Codoped Tellurite Glasses

Spectroscopic Properties of Er3+–Yb3+ Co-Doped Glass Ceramics Containing BaF2 Nanocrystals

Spectroscopic Properties of Er3+/Yb3+ Co-Doped 50sio2–20al2o3–30caf2 Glass and Glass Ceramics

Spectroscopic Properties Of Er3+ And Yb3+ Co-Doped Glass Ceramics Containing Srf2 Nanocrystals

Research on optical properties of Yb3+/Er3+ co-doped oxy-fluoride glass

Spectroscopic Properties Of Er3+ Doped Glass Ceramics Containing Sr2gdf7 Nanocrystals

Spectroscopic properties of Er<sup>3+</sup>and Yb<sup>3+</sup>co-doped glass ceramics containing SrF<sub>2</sub>nanocrystals

Spectroscopic Properties of Er3+/Yb3+-codoped PbO–Bi2O3–Ga2O3–GeO2 Glasses

Spectroscopic Properties Eu3+ Doped and Tm3+/Yb3+ Codoped Oxyfluoride Glass Ceramics Containing Ba2GdF7 Nanocrystals

Spectral Analysis of Er3+-, Er3+/Yb3+- and Er3+/Tm3+/Yb3+-doped TeO2–ZnO–WO3–TiO2–Na2O Glasses

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

Structural and Upconversion Fluorescence Properties of Er3+/Yb3+-codoped Oxychloride Lead–germanium–bismuth Glass

Thermal Analysis And Optical Properties Of Yb3+/Er3+-Codoped Oxyfluoride Germanate Glasses

Spectroscopic Properties and Energy Transfer in Ga2O3–Bi2O3–PbO–GeO2 Glasses Doped with Er3+ and Tm3+

Effect of Yb3+concentration on Upconversion Emission of Er3+-doped Tellurite Glass

Spectroscopic Properties Of Erbium-Doped Bismuth Based Glasses At 1.54 Mu M

Spectroscopic Properties of New Erbium-Doped Tellurite Glass