The Structure, Magnetic and Magnetocaloric Effect of Misch-Metal (mm)2fe17−xalx (x = 0–2) Compounds
Wen-Liang Zuo,Adil Murtaza,Chao Zhou,Yin Zhang,Fanghua Tian,Sen Yang,Feng-Xia Hu,Bao-Gen Shen
DOI: https://doi.org/10.1016/j.jmmm.2020.166487
IF: 3.097
2020-01-01
Journal of Magnetism and Magnetic Materials
Abstract:In this study, the structural, magnetic and magnetocaloric effects (MCE) of misch-metal (MM)(2)Fe17-xAlx (0 <= x <= 2) compounds are investigated. The XRD patterns indicate that all the samples crystallize primarily in a rhombohedral Th2Zn17 type crystal structure coexisting with a small amount of precipitation phase alpha-Fe. The lattice parameters and the Curie temperature (T-C) increase linearly with the increase of Al content. This allows the (MM)(2)Fe(17-x)Al(x )compounds to achieve magnetic refrigeration over the entire room temperature range. The maximum values of entropy changes (Delta S-M ) for (MM)(2)Fe17-xAlx (x = 0, 0.5, 1 and 1.5) compounds with a magnetic field variation of 0-2 T and 0-5 T are determined to be - 2.1 J Kg(-1) K-1, -1.3 J Kg(-1) K-1, -1.9 J Kg(-1) K-1, 1.9 J Kg(-1) K-1 and - 4.0 J Kg(-1) K-1, -2.7 J Kg(-1) K-1, -3.5 J Kg(-1) K-1, -3.5 J Kg(-1) K-1, respectively. The relative cooling power (RCP) for all the studied compounds is larger than 90 and 270 Jkg(-1) while the full-width half maxima (delta T-FWHM) is larger than 60 K and 100 K with the field changes of 0-2 T and 0-5 T, respectively. These results indicate that (MM)(2)Fe17-xAlx (0 <= x <= 2) compounds could have higher magnetocaloric cost-performance comparable to the room-temperature magnetic refrigeration materials R2Fe17 (R = Pr, Nd) and Gd with the second-order phase transition (SOPT).