Abstract:Cerium dioxide (CeO2) nanoparticles were synthesized by sol–gel-based hydrothermal method. During synthesis, cerium(III) chloride heptahydrate (CeCl3⋅7H2O) was used as cerium source; ammonia (NH3), tetraethylammonium hydroxide (C8H21NO), tetra-n-butyl ammonium hydroxide (C16H37NO), benzyl trimethyl ammonium hydroxide (C10H17NO) and benzyl triethyl ammonium hydroxide (C13H23NO) ionic liquids were used as catalyst, deionized water (H2O) was used as hydrolysis agent and solvent, and 2-aminopropanoic acid (C3H6NO2) was used as stabilizing agent. The nano-CeO2 particles were characterized by several techniques X-ray diffractometer (XRD), particle size analyzer, Branauer–Emmett–Teller analyzer (BET), ultraviolet–visible spectrophotometer (UV–Vis), transmission electron microscope (TEM). XRD characterization confirms that CeO2 crystals were analyzed as cubic fluorite structure. The full width at half maximum (FWHM) values referring to [111] lattice planes of CeO2 indicate a decrease in crystallinity associated with different bases used during synthesis of particles. Small sized crystals were formed in weak ionization degree and branched structures. As the crystallite size decreases, both agglomeration and the hydrodynamic diameter increases as expected. The size distribution of nano-CeO2 particles obtained by precipitation using different bases with a pH of 10 decreases from 25.92 to 20.57 nm. The size of nanoparticles prepared using ammonia at pH 9 and 8 are 15.60 and 9.50 nm, respectively. The most significant surface area change occurred in particles obtained using benzyl trimethyl ammonium hydroxide (BTMAH) and benzyl triethyl ammonium hydroxide (BTEAH). Such a significant reduction in surface area is believed to be due to the agglomeration or aggregation of particles with small crystallite size, resulting in smaller sized crystals as the alkyl group chain length and branching increase. These irregularities may result from the agglomeration and formation of large clusters observed by the TEM. The obtained CeO2 nanoparticles are crystalline and can readily be dispersed in water without any additional processing or surfactant agent. Well-defined strong absorbance peak located at 200–800 nm was observed for all samples. The bandgap increases with the decrease in particle size, meaning that smaller particles exhibit better UV absorption. The fact that the particles obtained in the presence of BTMAH and BTEAH cut off longer wavelength proved that it is due to lower bandgap energies.Graphical abstract

Sonochemical Synthesis of Cerium Oxide Nanoparticles - Effect of Additives and Quantum Size Effect

Synthesis of Cerium Oxide Nanoparticles by the Precipitation Method

Synthesis and Crystallization of Nano-Ceria Particles by Solvothermal Routes

Preparation of ceria by combined sol–gel and hydrothermal method: insights from the effects of different bases on the particle size distribution

CeO2 nanocrystals: Seed-mediated synthesis and size control

Preparation of Nanometer Cerium Oxide by Microwave Irradiation and Study on Its Surface Modification

Preparation of nano-sized CeO2 by mechanochemical reaction of cerium carbonate with sodium hydroxide

Synthesis of Cerium(IV) Oxide Ultrafine Particles by Solid‐State Reactions

Synthesis of quantum-size cerium oxide nanocrystallites by a novel homogeneous precipitation method

Wet chemical preparation of well-dispersed colloidal cerium oxide nanocrystals

Size controlled synthesis of CeO2 nanoparticles by a microemulsion method

Characterization of CeO 2 Fine Particles Prepared by the Homogeneous Precipitation Method with a Mixed Solutionof Ethylene Glycol and Polyethylene Glycol

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

The Synthesis of Nanometer Sized CeO2 Particles by the Coupling Route of Microemulsion with Homogeneous Precipitation

Synthesis and characterisation of CeO2 nanoparticles and rods

Formation and Thermal Decomposition of Cerium‐Organic Precursor for Nanocrystalline Cerium Oxide Powder Synthesis

Facile Synthesis of Ceria Nanocrystals with Tuneable Size and Shape

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology

Wet Chemical Synthesis of Nanometer CeO2 with Strong Ultraviolet Absorption Property by in Situ Assembly of Hybrid Precursors

Revealing the Effect of Synthesis Conditions on the Structural, Optical, and Antibacterial Properties of Cerium Oxide Nanoparticles

Fast Synthesis Of Cerium Oxide Nanoparticles And Nanorods