Template synthesis of single-crystal Cu nanowire arrays by electrodeposition

T. Gao,G.W. Meng,J. Zhang,Y.W. Wang,C.H. Liang,J.C. Fan,L.D. Zhang

DOI: https://doi.org/10.1007/s003390100910

2001-01-01

Applied Physics A

Abstract:. Cu nanowire arrays have been synthesized using potentiostatic electrodeposition within the confined nanochannels of a porous anodic alumina membrane. The Cu nanowire arrays and the individual nanowires have been characterized using SEM, TEM, SAED, HREM and XRD. Investigation results reveal that the Cu nanowire arrays having high wire packing densities are highly ordered over large areas. The individual Cu nanowires (diameter ∼60 nm) were single-crystal and found to be dense and continuous with uniform diameters throughout their entire length. An optimum ECD condition (at lower overpotentials) for the synthesis of single-crystal Cu nanowires was also discussed.