Oxygen Delignification of Kraft Eucalyptus Pulp
LI Rui-rui,LI Jun,WU Hui-min,XU Jun
DOI: https://doi.org/10.3969/j.issn.1007-9211.2011.10.007
2010-01-01
Abstract:Oxygen delignification of Eucalyptus kraft pulp and their performance were studied in this paper, focusing on the effects of oxygen delignification on unscreened pulp, screened pulp and the pulp washing with filtrate, as well as conducted fiber analysis. The results showed that the best oxygen delignification process on Eucalyptus KP pulp as follows, the dose of alkali was 4.0%(relative to dry, as below), the time was 80 min, pulp consistency was 10%, the temperature was 100℃, the oxygen pressure was 0.5MPa, and 0.5% MgSO4 during the oxygen bleaching as a protecting agent for carbohydrates. Pulp obtained at this condition, the brightness was 54.48% ISO, viscosity was 688.5mL·g-1, Kappa number was 10.39. The pulp washing with filtrate and unscreened pulp were better than the screened pulp after oxygen delignification, the pulp washing with filtrate had the highest brightness, and the add rate of brightness was 18.3%, lignin removal rate and the yield of unscreened pulp were the highest, they were 47.3%, 96.7% respectively. These types of pulps were almost no difference in fiber length and the coarseness changed little after oxygen delignification.