Formation and optical properties of copper nanoclusters in a silicate glass

Jian Zhang,Jiawei Sheng

DOI: https://doi.org/10.1016/j.ijhydene.2009.02.032

IF: 7.2

2009-01-01

International Journal of Hydrogen Energy

Abstract:In this letter, copper nanoclusters formation was observed in Cu-doped silicate glasses after UV-light irradiation followed by thermal annealing. After heating at 460°C for 45min, the Cu nanoclusters formed only in the UV-light irradiated glass, but not appeared in the un-irradiated sample. The critical temperature around at 460°C was found in the irradiated sample to form Cu nanoclusters. Thermal annealing at the temperature above this critical point would form Cu nanoclusters both in the irradiated and un-irradiated glasses. Compared to the un-irradiated sample, the UV-light irradiated glass usually had more free electrons, and then more Cu+ could trap electrons to form atoms.