Abstract:Superconductivity is observed in a new nontoxic cuprate system Ga-Ba-Ca-Cu-O, with Tc = 82K for GaBa2Ca5Cu6O14+{\delta} (Ga-1256) and Tc = 116K probably for GaBa2Ca3Cu4O10+{\delta} (Ga-1234) or GaBa2Ca2Cu3O8+{\delta} (Ga-1223), respectively. All compounds are fabricated by solid state reaction method under high pressure and high temperature. Samples are characterized by resistivity, magnetization and X-ray diffraction (XRD) measurements. The temperature dependence of magnetization measured in both zero-field-cooled and field-cooled processes on one sample (S1) shows two superconducting transitions at about 82K and 113K. The estimated shielding fraction for the phase with Tc of 82K is about 67%, while the fraction for another phase with Tc of 113K is quite small. The XRD Rietveld refinement for S1 indicates two main phases existing in the sample, Ga-1256 with fraction of about 58% and non-superconducting Ca0.85CuO2 with fraction of about 42%, respectively. Thus, we can conclude the superconducting phase with transition temperature of 82K is due to Ga-1256. The resistivity measurement also confirms the superconductivity for S1, and the resistivity reaches zero at about 82K. The temperature dependence of magnetization for another sample (S2) shows much higher superconducting shielding fraction for the phase with Tc of 116K, which may be a promising prospective for the synthesis of Ga-1234 or Ga-1223 phase.

A New Superconducting Oxide GdBaCuO with Tc (ρ=0) above 92K

Superconducting Oxide Dy-Ba-Cu-O with TC(π=0) Beyond 90K

The Superconducting Oxide Group with Zero-Resistance Temperature above 90-K

High T/sub C/ Superconductivity of (ba,y)cuo/sub 3/

Zero Resistance above 90K in Superconducting Oxide Tm-Ba-Cu-O

Discovery of a new nontoxic cuprate superconducting system Ga-Ba-Ca-Cu-O

High Tc superconductivity in LnBa2Cu3O7−y(Ln=Y, Gd, Dy, Yb) single crystal with large size

High-Tc Superconductivity In Yba2cu3o7-Y, Gdba2cu3o7-Y, Ybba2cu3o7-Y Single-Crystal With Large Size

Synthesis and Superconductivity of A New Type of 1212 Phase Cuprate (B,cd)(sr,ba)(2)ycu2oy

High-Tc Superconductivity And S-I Transition In Ba-Y-Cu-O

Effects of Solid Solutions on the Superconducting Properties of Gd–Ba–Cu–O Superconductors

A new superconductor in lead cuprate (Pb0.5Ba0.5)Sr2(Y0.5Ca0.5)Cu2Oy

Out of plane effect on the superconductivity of Sr2-xBaxCuO3+y with Tc up to 98K

Zero Resistance above 90K in Superconducting Oxides ErBaCuO and YbBaCuO

Antiferromagnetic Ordering in the High-Tc Superconductors (y1−xgdx) Ba2Cu3O7−y

The Synthesis and Characterization of HgBa2Ca2Cu3O8+δ Superconductors with Substitution of Hg by Pb

SUPERCONDUCTIVITY IN THE U-Y-Ba-Cu-O SYSTEM

Preparation and Superconducting Properties of the (cu,c)ba2ca3cu4o11+y Films with Zero-Resistance Transition Temperature of 96 K

Raman and Infrared Spectra of High Tc Superconducting Systems YBa2Cu3−xCoxO7−δ

Superconductivity at 94 K in HgBa2Cu04+δ

High-Tc superconductivities and electronic structures of some (BaxY1−x)CuO3 species by x-ray photoelectron spectroscopy