Remarkable effect of the incorporation of titanium on the catalytic activity and SO2 poisoning resistance of magnetic Mn–Fe spinel for elemental mercury capture

Shijian Yang,Yongfu Guo,Naiqiang Yan,Daqing Wu,Hongping He,Jiangkun Xie,Zan Qu,Jinping Jia

DOI: https://doi.org/10.1016/j.apcatb.2010.11.012

2011-01-01

Abstract:Tiantium (Ti) was incorporated into non-stoichiometric Mn–Fe spinel to improve its performance for elemental mercury capture. Although the number of Mn4+ cations on (Fe2TixMn1−x)1−δO4 was less than that on the corresponding (Fe3−xMnx)1−δO4, the number of usable cation vacancies for elemental mercury oxidization obviously increased. As a result, elemental mercury capture by Mn–Fe spinel was generally promoted by the incorporation of Ti. Furthermore, SO2 mainly reacted with ≡FeIII–OH and few Mn4+ cations on the surface reacted with SO2 at lower temperatures (100–150°C), so SO2 poisoning resistance improved at lower temperatures due to the incorporation of Ti. Especially, (Fe2Ti0.5Mn0.5)1−δO4 showed an excellent capacity (4.2mgg−1) for elemental mercury capture in the presence of a high concentration of SO2 at 150°C. Meanwhile, (Fe2Ti0.5Mn0.5)1−δO4 with the saturation magnetization of 30.6emug−1 can be readily separated from the fly ash using magnetic separation, leaving the fly ash essentially free of catalyst and adsorbed HgO. Therefore, nanosized (Fe2Ti0.5Mn0.5)1−δO4 may be a promising candidate catalyst for elemental mercury capture.