Abstract:The macrosegregation evolution kinetics of undercooled Cu 60 Fe 40 immiscible alloy during slow cooling and rapid cooling processes were investigated by laser heating and glass fluxing techniques. The critical undercooling for the occurrence of metastable phase separation (MPS) was determined as 41 K. As the undercooling rised, MPS always occurred even if the undercooling rised to the largest value of 482 K (0.28 T L ) and the nucleation temperature of primary phase was below the peritectic temperature for the first time. Meanwhile, both the phase separation time and the volume fraction of Fe-rich zone gradually increased under the two conditions. However, the phase separation time and the volume fraction of Fe-rich zone under the laser heating condition were much smaller than that under the glass fluxing state. At slight undercoolings, MPS preferentially happened at the bottom region of laser-heated sample and glass-fluxed sample, and the microstructure in other regions appeared as well-defined α Fe dendrites in the (Cu) matrix phase. In highly undercooled state, macrosegregation morphologies composed of floating Fe-rich zones and sinking Cu-rich zones were preserved. The critical undercooling for the macrosegregation formation of glass-fluxed sample was relatively larger. Moreover, the Fe-rich zone completely floated to the top of glass-fluxed sample while that located in the middle region of laser-heated sample. The higher the bulk undercooling, the lower the lattice constant of (Cu) phase and the greater the lattice constant of α Fe phase. The calculations and analyses of temperature field and fluid dynamics demonstrated that the difference of heat transfer mechanisms between laser-heated sample and glass-fluxed sample was responsible for the distinctions of macrosegregation evolution kinetics in the two experiments.

Microstructure evolution of undercooled iron–copper hypoperitectic alloy

A comparative study of macrosegregation evolution kinetics for undercooled Cu60Fe40 immiscible alloy during slow cooling and rapid cooling processes

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Effect of Minor Addition of Co on Nonequilibrium Solidification of Deeply Undercooled Cu Based Alloys

Rapid Solidification Structure Refinement Mechanism in Highly Undercooled Cu Based Ternary Alloys

A comparative study of metastable phase separation for undercooled liquid Fe35Cu65 alloy under natural and forced cooling conditions

Evolution Mechanism of Rapid Solidification Microstructure of an Undercooled Copper-Based Single Phase Alloy

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Microstructure Evolution in Undercooled Fe-7.5 At% Ni Alloys

Microstructure evolution and metastable phase formation in undercooled Fe–30 at.% Co melt

Solidification Microstructure Evolution and Grain Refinement Mechanism under High Undercooling of Undercooled Ni90Cu10 Alloys

Microstructural Evolution of Undercooled Fe83Ga17 Magnetostrictive Alloys

Formation of Single-Phase Supersaturated Solid Solution Upon Solidification of Highly Undercooled Fe–Cu Immiscible System

Direct Observation of Phase Transformation Layers in the Undercooled Hypoperitectic Ti47Al53 Alloy

Microstructure evolution of super-cooled Cu-Ni-Fe alloy

Effects of cooling rate on the microstructure control and liquid–liquid phase separation behavior of Cu–Fe–P immiscible alloys

Metastable phase formation and microstructure evolution in undercooled Fe-30Co alloy

The Microstructure Evolution of a Fe-Ni-P-B Soft Magnetic Alloy Solidified at Different Undercooling

Microstructural Transitions of Metastable Phase in Undercooled Fe–7.5 At% Ni Alloy

Solidification Structure Of Undercooled Alloys

Observations and simulations for phase separation process of immiscible Fe50Sn50 alloy droplets placed on a chilling surface