Abstract:Commercial silica support pellets were impregnated and calcined to contain cobalt oxide and ruthenium oxide for Fischer-Tropsch synthesis (FTS). The precatalyst pellets were split evenly into two groups, the control precatalyst (c-precat) and silylated precatalyst (s-precat), which were treated with 1H,1H, 2H, 2H-perfluorooctyltriethoxysilane (PFOS) in toluene. The samples of powderized s-precat were superhydrophobic, as determined by the water droplet contact angle (>150°) and sliding angle (<1°). Thermal analysis revealed the PFOS groups to be thermally stable up to 400 °C and temperature programmed reduction (TPR) studies showed that H2 reduction of the cobalt oxide to cobalt was enhanced at lower temperatures relative to the untreated c-precat. The two active catalysts were examined for their FTS performance in a tubular fixed-bed reactor after in situ reduction at 400 °C for 16 h in flowing H2 to give the active catalysts c-cat and s-cat. The FTS runs were performed under identical conditions (255 °C, 2.1 MPa, H2/CO = 2.0, gas hourly space velocity (GHSV) 510 h–1) for 5 days. Each catalyst was examined in three runs (n = 3) and the mean values with error data are reported. S-cat showed a higher selectivity for C5+ products (64 vs. 54%) and lower selectivity for CH4 (11 vs. 17%), CO2 (2 % vs. 4 %), and olefins (8% vs. 15%) than c-cat. S-cat also showed higher CO conversion, at 37% compared to 26%, leading to a 64% increase in the C5+ productivity measured as g C5+ products per g catalyst per hour. An analysis of the temperature differential between the catalyst bed and external furnace temperature showed that s-cat was substantially more active (DTinitial = 29 °C) and stable over the 5-day run (DTfinal = 22 °C), whereas the attenuated activity of c-cat (DTinitial = 16 °C) decayed steadily over 3 days until it was barely active (DTfinal < 5 °C). A post-run surface analysis of s-cat revealed no change in the water contact angle or sliding angle, indicating that the FTS operation did not degrade the PFOS surface treatment.

Study on Catalytic Performance and Attrition Strength of the Ruhrchemie Catalyst for the Fischer-Tropsch Synthesis in A Stirred Tank Slurry Reactor

Attrition Resistance and Catalytic Performance of Spray-Dried Iron Fischer−Tropsch Catalysts in a Stirred-Tank Slurry Reactor

Fischer–Tropsch Synthesis: Influence of CO Conversion on Selectivities, H 2 /CO Usage Ratios, and Catalyst Stability for a Ru Promoted Co/Al 2 O 3 Catalyst Using a Slurry Phase Reactor

Fischer–Tropsch Synthesis: Influence of CO Conversion on Selectivities, H<sub>2</sub>/CO Usage Ratios, and Catalyst Stability for a Ru Promoted Co/Al<sub>2</sub>O<sub>3</sub> Catalyst Using a Slurry Phase Reactor

Kinetics of the Fischer-tropsch Reaction over a Ru Promoted Co/al2o3 Catalyst

Attrition Studies of an Iron Fischer–Tropsch Catalyst Used in a Pilot-Scale Stirred Tank Slurry Reactor

Efficient and Stable Production of Long-Chain Hydrocarbons over Hydrophobic Carbon-Encapsulated TiO2-Supported Ru Catalyst in Fischer–Tropsch Synthesis

Catalytic Performance of Co-Ru/γ-Al2O3 Catalyst for Ficher-Tropsch Synthesis

Nanostructured Catalyst for Fischer-Tropsch Synthesis: Nanostructured Catalyst for Fischer-Tropsch Synthesis

Catalytic performance and attrition strength of spray-dried iron catalysts for slurry phase Fischer–Tropsch synthesis

Attrition Studies with Precipitated Iron Fischer–Tropsch Catalysts under Reaction Conditions

Fischer–Tropsch synthesis. Effect of CO pretreatment on a ruthenium promoted Co/TiO2

Effect of Ru Addition to Co/SiO2/HZSM-5 Catalysts on Fischer–Tropsch Synthesis of Gasoline-Range Hydrocarbons

Aqueous Phase Fischer–Tropsch Synthesis in a Continuous Flow Reactor

Superhydrophobic Surface Modification of a Co-Ru/SiO2 Catalyst for Enhanced Fischer-Tropsch Synthesis

Production of Lower Olefins with Highly Dispersed Ru Catalysts Supported on Al-SBA-15 in Fischer–Tropsch Synthesis

Ru catalysts supported by Si3N4 for Fischer-Tropsch synthesis

Modified Product Selectivity in Fischer-Tropsch Synthesis by Catalyst Pre-Treatment

Catalytic Properties of the Ru Promoted Co/SBA-15 Catalysts for Fischer–Tropsch Synthesis

Catalytic Performance of ZrO_2 Modified Co-Ru/γ-Al_2O_3 Catalyst for Fischer-Tropsch Synthesis

Studies on perfomence of Fischer - Tropsch synthesis over Fe - Cu - K catalyst