Abstract:With polyurethane as wall material, the preparation technology and process of microcapsule coating were studied on the surface of poly-α-olefin viscoelastic polymer particles. Molecular dynamics simulation methods were used to discuss the relevant molecular designs, and stable performance polyurethane microcapsules were produced by the method of interfacial polymerization, with toluene 2, 4-diisocyanate (TDI) and glycerol as active monomers. The influence on coating in monomer type, ratio, particle size and amount of wall material were researched, The surface morphology, oil solubility, heat and pressure resistance of poly-α-olefin microcapsules were tested. The influences of drag reduction effect by the indoor simulative loop evaluation system for oil drag reduction agent were evaluated. The results show that the length and number of branched chains had specific requirements in the design of coated wall material molecular. The reasonable process conditions of polyurethane-coated poly-α-olefin microcapsules were as follows: the system was aqueous solution, the molar ratio of isocyanate group (-NCO) and hydroxyl (-OH) was 1:1, the mesh number of poly-α-olefin particle size was 60-80 (250-180μm), the weight of wall material accounted for 0.5% of poly-α-olefin particles, the weight of surfactant accounted for 0.1% of poly-α-olefin particles, the temperature was 25°C under atmospheric pressure. The producing poly-α-olefin microcapsule had good surface morphology, faster release speed, no effect on the original drag reduction, excellent heat and pressure resistance. Moreover, poly-α-olefin microcapsules which were stored in powder-like solid at room temperature can be made into oil drag reduction agent easily at the time of on-site using by being dispersed into the solvent directly and solved the technical problem of dispersion in industrial applications.

Preparation of Polyurethane/Sandalwood Essential Oil Microcapsules with Interfacial Polymerization Method

Optimal Preparation and Characterization of Poly(urea–formaldehyde) Microcapsules

Preparation Of Olive-Oil/Polyurethane Microcapsules For Skin Care By Interfacial Polymerization

Preparation of Olive Oil-Polyurethane Microcapsules by Interfacial Polymerization

Preparation and Properties of Narrowly Dispersed Polyurethane Nanocapsules Containing Essential Oil Via Phase Inversion Emulsification

PREPARATION OF EXTRACTANT MICROCAPSULES BY SOLVENT EVAPORATION METHOD

Preparation of Microcapsules with Silicone Oil As Continuous Phase Using A Solvent Evaporation Method

Preparation and evaluation of microcapsules containing Rimulus Cinnamon and Angelica Sinenis essential oils

Study on Clove Oil Microcapsule with Montmorillonite /Polyurethane Hybrid Wall

Preparation of uniform microcapsules with silicone oil as continuous phase in a micro-dispersion process.

Preparation and Characterization of Silicone Oil/UF Resin Microcapsules as Erosion Inhibitor

Research on Preparation of Coated Poly-α-olefin Microencapsulation Based on Polyurethane

Direct In-Situ Polymerization for Preparing Microcapsules Based on Reactive Ethylene Silicon Oil Encapsulated by Poly(urea-Formaldehyde)

Studies on Syntheses, Structure and Morphology of Polyurethane Microcapsule

Preparation and Characterization of Microcapsulated Patchouli Oil

Versatile fabrication of nanocomposite microcapsules with controlled shell thickness and low permeability

Preparation and Characterization of Microcapsulated Patchouli Oil with Chitosan

Effect of surfactants on morphology and properties of microcapsules with hydrogen silicone oil encapsuled by PUF

Preparation of Mono-Dispersed Polyurea-Urea Formaldehyde Double Layered Microcapsules

Preparation of monosultap‐polyurethane microcapsules in an inverse emulsion through interfacial polymerization

Designing Polyurethane-based Microcapsule with Tailored Swelling Behaviours for Enhanced Oil Recovery